RCA.... e3 Vishay Automotive Grade, Sulfur Resistant Lead (Pb)-free Thick Film, Rectangular Chip Resistors FEATURES * Superior resistance against H2S-atmosphere * Automotive Grade = qualified according to AEC-Q 200 * Excellent stability (R/R 1 % for 1000 h at 125 C) * High volume product suitable for automotive applications * Metal glaze on high quality ceramic * Protective overglaze * Lead (Pb)-free solder contacts on Ni barrier layer * Pure tin plating provides compatibility with lead (Pb)-free and lead containing soldering processes * Compatible with "Restriction of the use of Hazardous Substances" (RoHS) directive 2002/95/EC (issue 2004) STANDARD ELECTRICAL SPECIFICATIONS SIZE MODEL INCH METRIC RCA0402 0402 POWER RATING P70 C W LIMITING ELEMENT VOLTAGE MAX V 0.063 50 1005 TEMPERATURE TOLERANCE RESISTANCE RANGE E-SERIES COEFFICIENT % ppm/K 100 200 200 1 1 5 10R - 10M 1R - 9R76 1R0 - 10M 24 + 96 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 1 5 1R0 - 2M2 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 1 5 1R0 - 10M 24 + 96 24 Zero-Ohm-Resistor: Rmax = 40 m Imax at 70 C = 1.2 A 0.10 RCA0603 0603 75 1608 100 200 Zero-Ohm-Resistor: Rmax = 40 m Imax at 70 C = 1.5 A 0.125 RCA0805 0805 150 2012 100 200 Zero-Ohm-Resistor: Rmax = 40 m Imax at 70 C = 1.7 A 0.25 RCA1206 1206 200 3216 100 200 Zero-Ohm-Resistor: Rmax = 20 m Imax at 70 C = 3.5 A 0.33 RCA1210 1210 200 3225 100 200 Zero-Ohm-Resistor: Rmax = 20 m Imax at 70 C = 4.0 A 1.0 RCA1218 1218 200 3246 100 200 Zero-Ohm-Resistor: Rmax = 20 m Imax at 70 C = 7.0 A 0.50 RCA2010 2010 400 5025 100 200 Zero-Ohm-Resistor: Rmax = 20 m Imax at 70 C = 5.0 A 1.0 RCA2512 2512 6332 500 100 200 Zero-Ohm-Resistor: Rmax = 20 m Imax at 70 C = 7.0 A Notes * These resistors do not feature a limited lifetime when operated within the permissible limits. However, resistance value drift increasing over operating time may result in exceeding a limit acceptable to the specific application, thereby establishing a functional time * Marking and packaging: see appropriate catalog or web pages * Power rating depends on the max. temperature at the solder point, the component placement density and the substrate material www.vishay.com 1 For technical questions in Europe, contact: ff3cresistors@vishay.com For technical questions in Americas/Asia, contact: ff2bresistors@vishay.com Document Number: 20037 Revision: 14-Jun-07 RCA.... e3 Automotive Grade, Sulfur Resistant Lead (Pb)-free Thick Film, Rectangular Chip Resistors Vishay TECHNICAL SPECIFICATIONS PARAMETER UNIT RCA0402 Rated Dissipation at 70 C3) W 0.063 0.10 0.125 0.25 0.33 1.0 0.5 1.0 Limiting Element Voltage2) V 50 75 150 200 200 200 400 500 Insulation Voltage (1 min) Vpeak > 75 > 100 > 200 > 300 > 300 > 300 > 300 > 300 Thermal Resistance1) K/W 870 550 440 220 140 65 88 65 Insulation Resistance > 109 Category Temperature Range C - 55 to + 125 (+ 155) Failure Rate h-1 0.3 x 10-9 29.5 25.5 40.5 Weight/1000 pcs g RCA0603 RCA0805 RCA1206 0.65 2 5.5 RCA1210 RCA1218 10 16 RCA2010 RCA2512 Notes 1. For sizes 0402 until 1206 the measuring conditions are in acc. to EN 140401-802. For all other sizes the result depends on the solder pad dimensions. 2. Rated voltage: PxR 3. The power dissipation on the resistor generates a temperature rise against the local ambient, depending on the heat flow support of the printed-circuit board (thermal resistance). The rated dissipation applies only if the permitted film temperature of 155 C is not exceeded. PART NUMBER AND PRODUCT DESPRIPTION PART NUMBER: RCA080510K0FKEA1) R C A 0 8 0 5 1 0 K 0 F K E A MODEL VALUE TOLERANCE TCR PACKAGING2) SPECIAL RCA0402 RCA0603 RCA0805 RCA1206 RCA1210 RCA1218 RCA2010 RCA2512 R = Decimal K = Thousand M = Million 0000 = 0 Jumper F=1% J=5% Z = Jumper K = 100 ppm/K N = 200 ppm/K 0 = Jumper S = Special EA EB EC ED EE EG EH EK EY up to 2 digits 100 ET1 e3 PRODUCT DESCRIPTION: RCA0805 10K 1 % 100 ET1 e3 RCA0805 10K 1% MODEL RESISTANCE VALUE TOLERANCE TCR PACKAGING2) LEAD (Pb)-FREE RCA0402 RCA0603 RCA0805 RCA1206 RCA1210 RCA1218 RCA2010 RCA2512 10R = 10 10K = 10 k 1M = 1 M 0R0 = Jumper 1% 5% 100 ppm/K 200 ppm/K ET1, ET5 ET6, ET7 EF4, E02 E67, E82 EG1, ET9 E20, E27 e3 = Pure Tin Termination Finish Notes 1. Preferred way for ordering products is by use of the PART NUMBER. 2. Please refer to table PACKAGING, see next page. Document Number: 20037 Revision: 14-Jun-07 For technical questions in Europe, contact: ff3cresistors@vishay.com For technical questions in Americas/Asia, contact: ff2bresistors@vishay.com www.vishay.com 2 RCA.... e3 Automotive Grade, Sulfur Resistant Lead (Pb)-free Thick Film, Rectangular Chip Resistors Vishay PACKAGING REEL MODEL BULK PACKAGING CODE TAPE WIDTH DIAMETER PITCH PIECES/ REEL PART NUMBER PAPER RCA0402 8 mm RCA0603 8 mm RCA0805 8 mm RCA1206 RCA1210 8 mm BLISTER PACKAGING CODE PRODUCT DESC. PAPER 180 mm/7" 2 mm 10 000 ED 285 mm/11.25" 2 mm 20 000 EC ET6 330 mm/13" 2 mm 50 000 EE EF4 180 mm/7" 4 mm 5000 EA 4 mm 10 000 EB 330 mm/13" 4 mm 20 000 EC EL ET6 E20 EI ET1 EI ET1 EG1 4 mm 5000 EA 4 mm 10 000 EB 330 mm/13" 4 mm 20 000 EC EL ET6 E20 EI ET1 EG1 5000 EA 4 mm 10 000 EB 330 mm/13" 4 mm 20 000 EC 180 mm/7" 4 mm 5000 EA 12 mm 285 mm/11.25" 50 000 EY E27 25 000 EY E27 10 000 EY E27 EG1 180 mm/7" 4 mm PRODUCT DESC. ET5 285 mm/11.25" 180 mm/7" PART NUMBER ET7 285 mm/11.25" 285 mm/11.25" PIECES BLISTER ET5 ET5 EL ET6 E20 ET1 4 mm 10 000 EB ET5 330 mm/13" 4 mm 20 000 EC ET6 RCA1218 12 mm 180 mm/7" 4 mm 4000 EK ET9 RCA2010 12 mm 180 mm/7" 4 mm 4000 EF E02 RCA2512 12 mm 180 mm/7" 8 mm 2000 EG E67 4 mm 4000 EH E82 DIMENSIONS SIZE DIMENSIONS [in millimeters] INCH METRIC 0402 L W H T1 INCH METRIC a b l 0402 1005 0.4 0.6 0.5 1.0 0.05 0.5 0.05 0603 1608 1.55 + 0.10 0.85 0.1 - 0.05 0805 2012 2.0 + 0.20 1206 3216 3.2 + 0.10 - 0.20 1.6 0.15 1210 3225 3.2 0.2 1218 3246 3.2 + 0.10 2010 5025 5.0 0.15 2.5 0.15 0.6 0.1 0.6 0.2 0.6 0.2 2512 6332 6.3 0.2 3.15 0.15 0.6 0.1 0.6 0.2 0.6 0.2 - 0.20 www.vishay.com 3 SOLDER PAD DIMENSIONS [in millimeters] REFLOW SOLDERING WAVE SOLDERING 0.2 0.1 1005 - 0.10 0.35 0.05 0.25 0.05 SIZE T2 a b l 0.45 0.05 0.3 0.2 0.3 0.2 0.3 + 0.20 0603 1608 0.5 0.9 1.0 0.9 0.9 1.0 1.25 0.15 0.45 0.05 0.3 0.2 0805 2012 0.7 1.3 1.2 0.9 1.3 1.3 0.55 0.05 0.45 0.2 0.4 0.2 1206 3216 0.9 1.7 2.0 1.1 1.7 2.3 2.5 0.2 0.55 0.05 0.45 0.2 0.4 0.2 1210 3225 0.9 2.5 2.0 1.1 2.5 2.2 1218 3246 1.05 4.9 1.9 1.25 4.8 1.9 4.6 0.15 0.55 0.05 0.45 0.2 0.4 0.2 2010 5025 1.0 2.5 3.9 1.2 2.5 3.9 2512 6332 1.0 3.2 5.2 1.2 3.2 5.2 - 0.10 For technical questions in Europe, contact: ff3cresistors@vishay.com For technical questions in Americas/Asia, contact: ff2bresistors@vishay.com Document Number: 20037 Revision: 14-Jun-07 RCA.... e3 Automotive Grade, Sulfur Resistant Lead (Pb)-free Thick Film, Rectangular Chip Resistors Vishay Percentage of Samples with Visually Detected Silver Sulfide Crystals, % FUNCTIONAL PERFORMANCE Saturated Sulfur Vapor (90 C, 72 % RH) 100 CRCW0603 80 60 RCA0603 40 20 0 0 500 1000 1500 2000 2500 3000 3500 Exposure time in hours Rated Power in % Derating 120 100 80 60 40 20 0 - 55 - 25 0 25 50 75 100 125 150 175 70 Ambient Temperature in C Temperature Rise in C Temperature Rise 90 80 0402 0603 0805 1206 1210 70 60 50 2010 40 2512 30 1218 20 10 0 0 0.1 0.2 0.3 0.4 0.5 Power in Watts Document Number: 20037 Revision: 14-Jun-07 For technical questions in Europe, contact: ff3cresistors@vishay.com For technical questions in Americas/Asia, contact: ff2bresistors@vishay.com www.vishay.com 4 RCA.... e3 Vishay Automotive Grade, Sulfur Resistant Lead (Pb)-free Thick Film, Rectangular Chip Resistors TEST PROCEDURES AND REQUIREMENTS AEC-Q 200 TEST (clause) REQUIREMENTS PERMISSIBLE CHANGE (R/R) CONDITIONS OF TEST stability for product types: 1 to 10 M 1 to 10 M 1% 5% 100 ppm/K 200 ppm/K RCA.... e3 Resistance - Electrical characterization (19) Parametrically test per lot and sample size requirements, summary to show Min, Max, Mean and Stand. Dev. at room as well as Min and Max operating temperatures Solderability (18) J-STD-002 Magnification 50 X a) Method B, 4 hours at 155 C dry heat at 235 C b) Method B at 215 C cat. 3 c) Method D cat. 3 at 260 C Resistance to soldering heat (15) MIL-STD-202 Method 210 260 C; 10 s, 25 mm/s, single dip Thermal shock (16) MIL-STD-202 Method 107 - 55 C/+ 125 C, 300 cycles Dwell time 15 min Transfer time 20 sec Air to Air ( 1 % R + 0.05 ) Moisture resistance (6) MIL-STD-202 Method 106 t = 24 hours/cycle Steps 7a & 7b not required Unpowered Measurements at 24 2 hours after test conclusion ( 1 % R + 0.05 ) Biased humidity (7) MIL-STD-202 Method 103 1000 hours; + 85 C/85 % RH 10 % of operating power Measurements at 24 2 hours after test conclusion ( 1 % R + 0.05 ) Operational life (8) MIL-STD-202 Method 108 1000 hours; 125 C; Rated Power Measurements at 24 2 hours after test conclusion ( 1 % R + 0.05 ) High temperature exposure (3) MIL-STD-202 Method 108 1000 hours at 125 C Unpowered Measurements at 24 2 hours after test conclusion ( 1 % R + 0.05 ) Humid Sulfur Vapor Test ASTM B 809-95 Humid sulfur oven 60 2 C, 86-90 % RH, 480 hours Measurements at 1-2 hours after test conclusion and visual examination ( 1 % R + 0.05 ) 95 % covered with solder wetting ( 0.5 % R + 0.05 ) APPLICABLE SPECIFICATIONS * AEC-Q 200 Automotive Specification * IEC 60068-2-x Variety of environmental test procedures * IEC 60286-3 Packaging of SMD components * ASTM B 809-95 Standard Test Method for Porosity in Metallic Coatings by Humid Sulfur Vapor www.vishay.com 5 For technical questions in Europe, contact: ff3cresistors@vishay.com For technical questions in Americas/Asia, contact: ff2bresistors@vishay.com Document Number: 20037 Revision: 14-Jun-07 Legal Disclaimer Notice Vishay Notice Specifications of the products displayed herein are subject to change without notice. Vishay Intertechnology, Inc., or anyone on its behalf, assumes no responsibility or liability for any errors or inaccuracies. Information contained herein is intended to provide a product description only. No license, express or implied, by estoppel or otherwise, to any intellectual property rights is granted by this document. Except as provided in Vishay's terms and conditions of sale for such products, Vishay assumes no liability whatsoever, and disclaims any express or implied warranty, relating to sale and/or use of Vishay products including liability or warranties relating to fitness for a particular purpose, merchantability, or infringement of any patent, copyright, or other intellectual property right. The products shown herein are not designed for use in medical, life-saving, or life-sustaining applications. Customers using or selling these products for use in such applications do so at their own risk and agree to fully indemnify Vishay for any damages resulting from such improper use or sale. Document Number: 91000 Revision: 08-Apr-05 www.vishay.com 1