CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 1 OF 10
0805 Series Thin Film Chip Resistor
1. Scope
This specification applies to 1.25mm x 2.0mm (0805) size, fixed metal chip resistors rectangular
type for use in electronic equipment.
2. Type Designation
RR1220 X XXX X N
(1) (2) (3) (4)
(5)
Where (1) Series No.
(2) Tolerance of TCR :
P = ± 25ppm/
Q = ± 50ppm/
R = ± 100ppm/
(3) Nominal resistance value :
For example –-
Three digits of number (E-24 Series)
100 = 10
102 = 1k
Four digits of number (E-96 Series)
11R3 = 11.3
1131 =1.13k
(4) Resistance tolerance :
B = ± 0.1%
D = ± 0.5%
(5) N = Sn plating (Lead free , RoHS Compliant)
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 2 OF 10
3. Electrical Specifications
Power Rating* 1/10 W
Resistance Values E-24 series , E-96 series
Resistance Tolerance ± 0.5%(D) ± 0.1%(B) , ± 0.5%(D)
Resistance Range 1097.6 1001M 102k1M
T.C.R. (Temperature Coefficient
of Resistance) ± 50ppm∕℃ ± 25ppm∕℃ ± 25ppm∕℃
± 100ppm∕℃
Operating Temperature Range -55 to 125
Max. Operating Voltage** 100V
Note: *Package Power Temperature Derating Curve
Figure 1.Power Temperature Derating Cure
Note: **Resistors shall have a rated DC or AC(rms.) continuous operating voltage corresponding to the
power rating, as calculated from the following formula
W
here V : Rated voltage (V)
P : Rated power (W)
RPV ×=
R : Nominal resistance ()
If the voltage so obtained exceeds the maximum operating voltage, this maximum voltage shall
be the rated voltage.
0
-55 70 125
100
RATED LOAD(%)
AMBIENT TEMPERATURE( )
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 3 OF 10
4. Outline dimensions
5. Marking
5-1 Marking in E-24 Series :
A rated resistance shall be marked on the protect coating with three digits of number.
Example :
3.9k39 X 102392
5-2 Marking in E-96 Series :
A Manufacturing date code shall be marked on the protect coating.
Example :
10.2102 X 10-110R2
10.2k102 X 1021022
Code Letter Dimension
L 2.00 ± 0.2
W 1.25 ± 0.2
t 0.40 ± 0.1
a 0.40 ± 0.2
Unit : mm
L
W
a
a
t
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 4 OF 10
6. Life Tests
6-1 Electrical
Item Specification and Requirement Test Method
Short Time Overload R: ± (0.5%+ 0.05)
Without damage by flashover, spark,
arcing, burning or breakdown
(1) Applied voltage:
2.5 x rated voltage or
2 x maximum operating voltage
which ever is less
(2) Test time : 5 seconds
Insulation Resistance Over 100 M on Overcoat layer face
up
Over 1,000 M on Substrate side face
up
(1) Setup as figure 2
(2) Test voltage: 100 VDC
(3) Test time:
60 + 10 / -0 seconds
Voltage Proof R: ± (0.5%+ 0.05)
Without damage by flashover, spark,
arcing, burning or breakdown
(1) Setup as figure 2
(2) Test voltage: 100 VAC(rms)
(3) Test time:
60 +10 / -0 seconds
Figure 2 : Measurement Setup
Substrate Side
(R=0.5 mm)
Measurement Point A
Over coat Film
Pressure Rod
(Metal)
Substrate
Measurement Point B
Metal Block
Sample Electrode
Insulation Plate
B
A
Spring
Voltage Supply
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 5 OF 10
6-2 Mechanical
Item Specification and Requirement Test Method
Solderability The surface of terminal immersed shall
b
e minimum of 95% covered with a new
coating of solder
Solder bath:
After immersing in flux, dip in
245 ± 5 molten solder bath for
2 ± 0.5 seconds
Resistance to Solder
Heat
R: ± (0.5%+ 0.05)
Without distinct deformation in
appearance
(1) Pre-heat: 100~110 for
30 seconds
(2) Immersed at solder bath of
270 ± 5 for 10 ± 1 seconds
(3) Measuring resistance
1 hour after test
Vibration R: ± (0.5%+ 0.05)
Without mechanical damage such as
break
(1) Vibration frequency:
10Hz to 55Hz to10Hz in
60 seconds as a period
(2) Vibration time: period cycled for
2 hours in each of 3 mutual
perpendicular directions
(3) Amplitude: 1.5mm
Shock R: ± (0.25%+ 0.05)
Without mechanical damage such as
break
(1) Peak value: 490N
(2) Duration of pulse: 11ms
(3) 3 times in each positive and
negative direction of 3 mutual
perpendicular directions
Bending Test R: ±(0.5%+ 0.05)
Without mechanical damage such as
break
Bending value: 3 mm for
30 ± 1 seconds
Solvent Resistance Marking should be legible
Without mechanical and distinct damage
in appearance
(1) Solvent:
Trichloroethane
or Isopropyl alcohol
(2) Immersed in solvent at
room temperature for
90 seconds
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 6 OF 10
6-3 Endurance
Item Specification and Requirement Test Method
Rapid change of
Temperature
R: ± (0.5%+ 0.05)
Without distinct damage in
appearance
(1) Repeat 5 cycle as follow:
(-55 ± 3,30minutes) (Room
temperature, 2~3 minutes)
(+125 ± 2,30minutes)
(Room temperature, 2~3
minutes)
(2) Measuring resistance
1 hour after test
Moisture with Load R: ± (1.0%+ 0.05)
Without distinct damage in appearance
Marking should be legible
(1) Environment condition:
40 ± 2,90~95% RH
(2) Applied Voltage:
rated voltage
(3) Test period: (1.5 hour ON)
(0.5 hour OFF) cycled for
total1,000 + 48 / - 0 hours
(4) Measuring resistance
1 hour after test
Load Life R: ± (1.0%+ 0.05)
Without distinct damage in appearance
(1) Test temperature:
70 ± 2
(2) Applied Voltage:
rated voltage
(3) Test period: (1.5 hour ON)
(0.5 hour OFF) cycled for
total 1,000 + 48 / - 0 hours
(4) Measuring resistance
1 hour after test
Low Temperature
Store
R: ± (1.0%+ 0.05)
Without distinct damage in appearance
(1) Store temperature:
-55 ± 3 for total
1,000 + 48 / - 0 hours
(2) Measuring resistance
1 hour after test
High Temperature
Store
R: ± (1.0%+ 0.05)
Without distinct damage in appearance
(1) Store temperature:
+125 ± 2 for total
1,000 + 48 / - 0 hours
(2) Measuring resistance
1 hour after test
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 7 OF 10
7. Recommend Land Pattern Dimensions
A 0.8~1.0
B 3.0
C 1.1~1.3
Unit : mm
C
A
B
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 8 OF 10
8. Packaging
8-1 Dimensions
8-1-1 Tape packaging dimensions
8-1-2 Reel dimensions
A
P
P
B = 2.4 ± 0.2
P(PITCH) = 4.0 ± 0.1
0.75 ± 0.05
0.8 ± 0.1
CHIP
A = 1.65 ± 0.2
1.5
+0.1
-0.0
8 ± 0.3
3.5 ± 0.05
1.75 ± 0.1
Unit : mm
2.0 ± 0.05
Carrier cavity
B
Pulling direction
Sprocket hole
Label
13 ± 0.2
21 ± 0.8
13 ± 1.4
9 ± 0.3
50
180+0
-3
R1
2 ± 0.5
105
Unit : mm
60+1
-0
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 9 OF 10
8-2 Peel force of top cover tape
The peel speed shall be about 300 mm/minute
The peel force of top cover tape shall be between 0.1 to 0.7 N
8-3 Numbers of taping
5,000 pieces/reel
8-4 Label marking
The following items shall be marked on the production and shipping
Label on the reel.
8-4-1 Production Label
(1) Part No.
(2) Description
(3) Quantity
(4) Taping No.
8-4-2 Shipping Label
(1) *Customer's name
(2) *Customer's part No.
(3) Manufacturer's part No.
(4) Manufacturer's name
(5) Manufacturer's country
*Note : Item (1) and (2) are listed by request
8-5 Note
Manufactured by our joint company. ( Susumu Co., Ltd. )
165~180°
Top Cover Tape
0.1N~0.7N
CYNTEC CO., LTD.
乾坤科技股份有限公司
DOCUMENT : RC000000N
REVISION : A1
PAGE : 10 OF 10
9. Care note
9-1 Care note for storage
(1) Chip resistor shall be stored in a room where temperature and humidity must be
controlled. (temperature 5 to 35, humidity 45 to 85% RH) However, a humidity
keep it low, as it is possible.
(2) Chip resistor shall be stored as direct sunshine doesn’t hit on it.
(3) Chip resistor shall be stored with no moisture, dust, a material that will make solderability
inferior, and a harmful gas (Chloridation hydrogen, sulfurous acid gas, and sulfuration
hydrogen)
9-2 Care note for operating and handling
(1) It is necessary to protect the edge and protection coat of resistors from mechanical stress.
(2) Handle with care when printing circuit board (PCB) is divided or fixed on support body,
because bending of printing circuit board (PCB) mounting will make mechanical stress for
resistors.
(3) Resistors shall be used with in rated range shown in specification. Especially, if voltage more
than specified value will be loaded to resistor, there is a case it will make damage for
machine because of temperature rise depending on generating of heat, and increase
resistance value or breaks.
(4) In case that resistor is loaded a rated voltage, it is necessary to confirms temperature of a
resistor and to reduce a load power according to load reduction curve, because a temperature
rise of a resistor depends on influence of heat from mounting density and neighboring
element.
(5) Observe Limiting element voltage and maximum overload voltage specified in each
specification
(6) If there is possibility that a large voltage (pulse voltage, shock voltage) charge to resistor, it
is necessary that operating condition shall be set up before use.