CL21B225KOFNNNF - Samsung [Electro-Mechanics]

SPECIFICATION

 Supplier : Samsung electro-mechanics  Samsung P/N : CL31C471JIHNNNE

 Product : Multi-layer Ceramic Capa citor  Description : CAP, 470㎊, 1000V, ±5%, C0G, 1206

CL 31 C471 J I H N N N E

① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪

①Series Samsung Multi-layer Ceramic Capacitor

②Size 1206 (inch code) L: 3.2 ± 0.2 mm W: ± 0.2 mm

③Dielectric C0G ⑧Inner electrode

④Capacitance 470 ㎊Termination

⑤Capacitance ±5 %Plating (Pb Free)

tolerance ⑨Product Normal

⑥Rated Voltage 1000 V ⑩Special Reserved for future use

⑦Thickness 1.6 ± 0.2 mm ⑪Packaging Embossed Type,7"reel(2,000ea)

A. Samsung Part Number

1.6

Sn 100%

B. Samsung Reliability Test and Judgement condition

Capacitance Within specified tolerance 1㎒±10% 0.5~5Vrms

Q1000 min

Insulation More than 500Mohm㎌500±50 Vdc 60~120 sec.

Resistance

Appearance No abnormal exterior appearance Visual inspection

Withstanding No dielectric breakdown or of the rated voltage

Voltage mechanical breakdown

Temperature C0G

Characteristics (From -55℃ to 125℃, Capacitance change should be within ±30PPM/℃)

Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.

of Termination terminal electrode

Bending Strength Capacitance change : within ±5% Bending to the limit (1mm)

with 1.0mm/sec.

Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder

is to be soldered newly 245±5℃, 3±0.3sec.

(preheating : 80~120℃ for 10~30sec.)

Resistance to Capacitance change : within ±2.5% Solder pot : 270±5℃, 10±1sec.

Soldering heat Tan δ, IR : initial spec.

120%

Performance Test condition

Vibration Test Capacitance change : within ±2.5% Amplitude : 1.5mm

Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)

2hours  3 direction (x, y, z)

Moisture Capacitance change : within ±7.5% With rated voltage

Resistance Q : 200 min 40±2℃, 90~95%RH, 500 +12/-0 hours

IR : More than 25㏁·㎌

High Temperature Capacitance change : within ±3% Wit

of the rated voltage

Resistance Q : 350 min Max. operating temperature

IR : More than 50㏁·㎌1000+48/-0 hours

Temperature Capacitance change : within ±2.5% 1 cycle condition

Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃

→Max. operating temperature →25℃

5 cycles test

C. Recommended Soldering method :

Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )

* For the more detail Specification, Please refer to the Samsung MLCC catalogue.

Performance Test condition

100%