B72210S621K351 - EPCOS (TDK)

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 0/8

Form: FBLE3K/b

File name: S10K625G5S3_a.doc

MODIFICATIONS: New Issue

REMARKS:

signed: PE / Collins-Hunt signed: QS / Zödl

Prepared by Tony Sun Release signed: signed:

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 1/8

SIOV nomenclature:

S = Disk type

10 = Rated disk diameter

K = Tolerance of varistor voltage at 1mA : ±10%

625 = Max. operating voltage Vrms

G5 = Taping Style G5

S3 = Crim p styl e S3

Figure: Dimensions given in Millimet er s (mm)

Electrical data:

Maxi mum ra tings (Ta=85°C)

Max. Operating AC voltage VRMS = 625 V

Max. Operating DC voltag e VDC = 825 V

Surge current (8/20µs) 1 time Imax = 2500 A

Energy absorption (2ms) 1 time Wmax = 68,0 J

Average power dissipation Pmax =0,4 W

Characteristics (Ta=25°C)

Varistor voltage at 1mA VV= 1000 V ± 10%

Clamping volt age at 25 A (8/20µs) VC,max = 1650 V

Type. Capacitance at 1 kHz C = 90 pF

bmax = 12,0

hmax = 17,5

smax =7,5

e = 7,5 ± 0,8 2)

∅d = 0,8 ± 0,05

lmin =n.a.

1) seating plane in accordance with IEC

60717

2) measured above carrier tape

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 2/8

V/I Characteristic:

10 -5 10 -4 10 -3 10 -2 10 -1 10 010 110 210 310 4

5000

100

200

400

600

800

1000

2000

4000

VAR9152A

Derating:

1 x

2 x

10 x

10^2 x

10^3 x

10^4 x

10^5 x

10^6 x

inf..

0,1

100

1000

10000

10 100 1000 10000

t r [µ s ]

S10K385 ... 68

max.

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 3/8

Taping:

Package Unit: 500 pcs./reel

Lead spacing 7,5mm

dmax = 500mm

wmax = 72mm

f = 23 ± 1,0mm

n = 59mm (typ.)

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 4/8

Tape dimensions, in Millimeters (mm):

Definition Symbol Dimension Tolerance Remarks

Body diameter b 12,0 max

Body thickness s 7,5 max

Lead diameter d 0,8 ± 0,05

Sprocket hole pitc h Po12,7 ± 0,3 ± 1mm/20 sprocket

holes

Distance hole center

to lead center P18,95 ± 0,8

Lead spacing F 7,5 ± 0,8 measured above

carrier tape

Component deviation ∆hdepending on s

Component deviation ∆p0± 2,0 measured at top of

component body

Carrier tape width W 18,0 ± 0,5

Adhesive tape width Wo11,0 min Peel-off force ≥5N

Sprocket hole position W19, 0 + 0,75/

-0,5

Adhesive tape position W23,0 max

Distance hole center to

the

top of the component

H145,0 max

Seating plane height H016 ± 0,5

Hole diameter D04,0 ± 0,2

Total tape thick ness t 0,9 max

Cutting level L 11,0 max

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 5/8

Reliability Data:

Characteristics Test Methods/Description Specifications

EVaristor

Voltage The voltage between two terminals with the

specified measuring current applied is called Vv

(1 mADC @ 0.2 - 2 s).

To meet the

specified value.

Clamping

Voltage The maximum voltage between two terminals

with the specified standard impulse current

(8/20µs) illustr ated below applied.

TS Rise Time µs

Tr Decay time to half value µs

O1 Nominal start

Im Peak value

Peak

Trailing Edge

Leading

Edge

To meet the

specified value.

Surge current

derating,

8/20 µs

100 surge currents (8/20 µs), unipolar, interval

30 s, amplitude corresponding to derating curve

for 20 µs

| ∆ V/V (1 mA) |

≤ 10 % (measured

in direction of surge

current)

No visible damage

L Surge current

derating,

2 ms

100 surge currents (2ms), unipolar, interval

120s, amplitude corresponding to derating curve

for 2ms

| ∆ V/V (1 mA) |

≤ 10 % (measured

in direction of surge

current)

No visible damage

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 6/8

Characteristics Test Methods/Description Specifications

Tensile

strength After gradually applying the force specif ied

below and keeping the unit fixed for 10 seconds,

the terminal shall be visually examined for any

damage.

Terminal diameter Force

0.5 mm 5 N

0.6 mm 10 N

0.8 mm 10 N

1.0 mm 20 N

| ∆ V/V (1 mA) |

≤ 5 %

No break of solder

joint, no wire break

Vibration Aft er r epeatedly applying a single harmonic

vibration according to the table below.

Thereafter, the unit shall be visually examined.

frequency range: 10 .... 55 Hz

amplitude: 0.75 mm or 98 m/s²

duration: 6 h (3 x 2 h)

pulse: sine wave

| ∆ V/V (1 mA) |

≤ 5 %

No visible damage

Solderability Afte r dipping t he terminals t o a depth of

approximately 3 mm from the body in a

soldering bath of 235°C for 5 seconds, the

terminals shall be visually examined.

The inspection shall

be carried out under

adequate light with

normal eyesight or

with the assistance

of a ma gnifier

capable of giving a

magnification of 4

times to 10 times.

The dipped surface

shall be covered

with a smooth and

bright sol der coating

with no more than

small amounts of

scattered

imperfections such

as pinholes or un-

wetted or de-wetted

areas. These

imperfections shall

not be concentrated

in one area.

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 7/8

Characteristics Test Methods/Description Specifications

Resistance to

soldering heat Each lead shall be dipped into a solder bath

having a temperature of 260 ± 5°C to a point 2.0

to 2.5 mm from the body of the unit, be held

there for 10 ± 1 s and then be stored at room

temperature and normal humidity for 1 to 2

hours. The change of Vv and mechanical

damages shall be examined.

| ∆ V/V (1 mA) |

≤ 5 %

No visible damage

Electric strength 2500 VRMS, 10 s

The varistor is placed in a container holding 1.6

± 0.2 mm diameter metal balls such that only the

terminations of the varistor are protruding.

The specified voltage shall be applied between

both terminals of the specimen connected

together and the electrode inserted between the

metal balls.

No breakdown

Metal Oxide Varistor Disc type

SIOV-S10K625G5S3 Ordering code: B72210S0621K351

Data sheet

ISSUE DATE 03.06.03 ISSUE A PUBLISHER KH PE VAR PAGE 8/8

Characteristics Test Methods/Description Specifications

Ma x. AC

operating

voltage

After being continuously applied the maximum

allowable voltag e at 85 ± 2°C for 1000 hours,

the specimen shall be stored at room

temperature and normal humidity for 1 to 2

hours. Thereafter, the change of Vv shall be

measured.

| ∆ V/V (1 mA) |

≤ 10 %

Damp heat,

steady state The specimen shall be subjected to 40 ± 2°C, 90

to 95 % r.H. for 56 days without load and then

stored at room temperature and normal humidity

for 1 to 2 hours. Thereafter, the change of Vv

shall be measured.

| ∆ V/V (1 mA) |

≤ 10 %

Climatic

sequence The specimen shall be subjected to:

a) dry heat at +85°C, 16 h

b) damp heat, 1st cycle: 55°C, 93 % r.H., 24 h

c) cold, -40°C, 2 h

d) damp heat, additional

5 cycles: 55°C, 93 % r.H., 24 h/cycle

Then the specimen shall be stored at room

temperature and normal humidity for 1 to 2

hours. Thereafter, the change of Vv shall be

measured.

| ∆ V/V (1 mA) |

≤ 10 %

Fast

temperature

cycling

The temperature cycle shown below shall be

repeated 5 times. Then the specimen shall be

stored at room temperature and normal humidity

for 1 to 2 hours. The change of Vv and

mechanical damage shall be examined.

Step Temperature (°C) Period (min.)

1 -40 ± 3 30 ± 3

2 transition time < 10 s

3 85 ± 2 30 ± 3

| ∆ V/V (1 mA) |

≤ 5 %

No visible damage

Note: More details can be found in the data book 'SIOV Metal Oxide Varistors', Ordering No. EPC:

62002-7600

 EPCOS AG 2002. Reproduction, publication and dissemination of this data sheet, enclosures hereto and the information

contained therein without EPCOS' prior express consent is prohibited.

Purchase orders are subject to the General Conditions for the Supply of Products and Services of the Electrical and

Electronics Industry recommended by the ZVEI (German Electrical and Electronic Manufacturers' Association), unless

otherwise agreed.