PR100 1OZ - 3M - Datasheet.Live

Scotch-Weld™

Plastic and Rubber Instant Adhesi ves

PR5 •PR40 •PR100 •PR600 •PR600B •PR1500 •PR Gel

Product

Description 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesives are designed to give

exceptional performance on difficult-to-bond plastic and rubber substrates. These adhesives

may be bonded to like substrates or in combination with metal or composite substrates.

Superior performance is achie ved on materials such as heavily plasticized PVC, EPDM,

ABS, Nylon, Santoprene®

, and Viton®

Technical Data March, 2010

Specific Features • 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR5 is a very low viscosity,

high-speed bonding cyanoacrylate formulated for plastics and rubbers. It is

recommended for use on assemblies with very close-fitting parts and smooth, even

surfaces. It can be used to wick into bonding gaps of assembled parts.

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR40 is a low viscosity

cyanoacrylate adhesi ve which bonds close-fitting plastic or rubber parts quickly and with

high strength.

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesi ve PR100 (formerly SB04 or

SB14) is a general purpose, low viscosity bonder for rubber or plastic surfaces. It has

been tested and passed the requirements of Commercial Item Description A-A-3097,

Type II, Class 2 (formerly MIL-A-46050C).

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR600 is a medium viscosity

cyanoacrylate with some gap-filling capability. It will bond many common substrates

including plastics and rubbers. It has been tested and passed the requirements of

Commercial Item Description A-A-3097, Type II, Class 3 (formerly MIL-A-46050C).

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR600B is a black version of

3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR600.

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive PR1500 (formerly SB16) is

a high viscosity cyanoacrylate that can be used on plastic or rubber parts that do not fit

well together. It has excellent gap-filling characteristics and will not wick into

unwanted areas. It has been tested and passed the requirements of Commercial Item

Description A-A-3097, Type II, Class 3 (formerly MIL-A-46050C).

• 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesi ve PR Gel (formerly PR54) is a

fast curing, very high viscosity, gap-filling cyanoacrylate. Its gel formulation is suitable

for bonding poorly mating components and for porous substrates and can be used on

vertical surfaces as it will not drip or slump.

3M™Scotch-Weld™

Plastic and Rubber Instant Adhesi ves

PR5 •PR40 •PR100 •PR600•PR600B •PR1500 •PR Gel

1 ISO 3104/3105.

2 Brookfield RVT, ‘T-spindle’ C @ 2.5 rpm.

3 Brookfield RVT, ‘T-spindle’ C @ 20 rpm.

4 Brookfield LVF, Spindle 3 @ 30 rpm.

- 2 -

Typical Uncured

Physical Pr operties Note: The follo wing technical information and data should be considered representative or

typical only and should not be used for specification purposes.

3M™ Scotch-Weld™

Plastic and Rubber Instant Adhesives

PR5 PR40 PR100 PR600

PR600B

PR1500 PR Gel

Color Clear Clear Clear Clear Black Clear Clear

Base Ethyl Ethyl Ethyl Ethyl Ethyl Ethyl Ethyl

Hybrid Hybrid Hybrid Hybrid Hybrid Hybrid

Appearance Liquid Liquid Liquid Liquid Liquid Liquid Gel

Specific Gravity (g/ml) 1.05 1.06 1.06 1.07 1.07 1.08 1.10

Viscosity (cps) 2 - 6

34 - 44

80 - 120

510 - 510 - 1,275 - 50,000 -

660

1,650

90,000

7,000 -

20,000

Time to Handling 1 - 10 3 - 20 10 - 30 4 - 25 4 - 25 20 - 100 3 - 60

Strength (sec)

Full Cure Time (hr) 24 24 24 24 24 24 24

Typical Cured

Properties Note: The following technical inf ormation and data should be considered representati v e or

typical only and should not be used for specification purposes.

3M™ Scotch-Weld™

Plastic and Rubber Instant Adhesives

PR5 PR40 PR100 PR600

PR600B

PR1500 PR Gel

Temperature Range (°F) -65 to -65 to -65 to -65 to -65 to -65 to -65 to

180 180 180 180 180 180 180

Gap Fill (in) 0.002 0.004 0.006 0.006 0.006 0.008 0.020

Tensile Strength (psi) 2,900

2,900

4,900

4,600

– 2,900

–

Overlap Shear – – 3,100

2,900

– – 2,900

Strength (psi)

5 ASTM D2095.

6 ISO 6922 (grit-blasted steel).

7 ASTM D1002 (grit-blasted steel).

3M™Scotch-Weld™

Plastic and Rubber Instant Adhesi ves

PR5 •PR40 •PR100 •PR600•PR600B •PR1500 •PR Gel

- 3 -

Surface Preparation

For optimum strength structural bonds, paint, oxide films, oils, dust, mold release

agents, and all other surface contaminants must be completely removed. However,

the amount of surface preparation depends on the required bond strength and the

environmental aging resistance desired by the user. Typical quick surface preparation

would include wiping with a clean solvent (such as isopropyl alcohol*), abrading

the surface with a clean fine abrasive, and then wiping again with a clean solvent to

remove loose particles.

Directions for Use

1. Ensure that parts are clean, dry, and free from oil and grease.

2. A instant adhesive activator may be required if there are bonding gaps or

porous substrate surfaces, if substrates are low surface energy plastics

(e.g., polyethylene, polypropylene) or if substrates have acidic surfaces

(e.g., paper, leather).

3. Bond speed is typically very fast so ensure that parts are properly aligned before

dispensing.

4. Product is normally hand applied from the bottle. Apply sparingly to one surface

and press parts firmly together until handling strength is achieved. As a general

rule, as little cyanoacrylate as possible should be used. Over application will

result in slower cure speed and lower bond strength.

Cured Bond Characteristics

1. Full bond strength will typically be achieved within a 24 hour cure time.

2. Low humidity or low temperature conditions will slow do wn the cure rate.

3. After curing, 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesiv e bonds

are suitable for use up to about 180°F (82°C). At 180°F (82°C) the bonds will

be approximately 70% of the strength at room temperature and at 212°F

(100°C) about 50% of full strength.

4. Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term

humidity, moisture, or water immersion may affect the strength of a cured

cyanoacrylate bond depending on the substrates and the bond gap. Testing is

recommended to evaluate the effect.

*Note: When using solvents, extinguish all ignition sources, including pilot lights,

and follow the manufacturer’s precautions and directions for use.

Handling Information

Storage For short term storage (<30 days), k eep adhesive in a cool (60°F to 80°F [16°C to

27°C]), dry place out of direct sunlight. K eep containers tightly covered and free of

moisture. Refrigeration (40°F [4°C]) gi ves optimum long term storage stability.

Shelf Life 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesi ves can be expected to have

a shelf life of one year from the date of shipment from 3M when stored under

refrigerated conditions.

3M™Scotch-Weld™

Plastic and Rubber Instant Adhesi ves

PR5 •PR40 •PR100 •PR600•PR600B •PR1500 •PR Gel

- 4 -

3M and Scotch-Weld are trademarks of

3M Company.

Santoprene is a registered trademark of

ExxonMobil Chemical.

Viton is a registered trademark of

E.I. DuPont de Nemours Co.

Printed in U.S.A.

Recycled Paper

40% pr e-consumer

10% post-consumer

Refer to Product Label and Material Safety Data Sheet for health and safety information before using this

product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501.

Precautionary

Information

The technical information, recommendations and other statements contained in this document are

based upon tests or experience that 3M believes are reliable, but the accuracy or completeness of such

information is not guaranteed.

Technical Information

Unless an additional warranty is specifically stated on the applicable 3M product packaging or product

literature, 3M warrants that each 3M product meets the applicable 3M product specification at the time

3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR

IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF

MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE OR ANY IMPLIED WARRANTY

OR CONDITION ARISING OUT OF A COURSE OF DEALING, CUSTOM OR USAGE OF TRADE.

If the 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s

option, replacement of the 3M product or refund of the purchase price.

Warranty,

Limited Remedy,

and Disclaimer

Except where prohibited by law, 3M will not be liable for any loss or damage arising from the 3M product,

whether direct, indirect, special, incidental or consequential, regardless of the legal theory asserted,

including warranty, contract, negligence or strict liability.

Limitation of Liability

This product was manufactured under a quality system registered to ISO 9001:2000 standards.

ISO 9001: 2000

Many factors beyond 3M’s control and uniquely within user’s knowledge and control can affect the use

and performance of a 3M product in a particular application. Given the variety of factors that can affect

the use and performance of a 3M product, user is solely responsible for evaluating the 3M product and

determining whether it is fit for a particular purpose and suitable for user’s method of application.

Product Use

Industrial Adhesives and Tapes Division

3M Center, Building 225-3S-06

St. Paul, MN 55144-1000

800-362-3550 • 877-369-2923 (Fax)