SPECIFICATION * Supplier : Samsung electro-mechanics * Samsung P/N : CL03C6R2CA3GNNC * Product : Multi-layer Ceramic Capacitor * Description : CAP, 6.2, 25V, 0.25, C0G, 0201 A. Samsung Part Number Series 0201 Dielectric C0G Capacitance 03 C 6R2 C A 3 G N N C Samsung Multi-layer Ceramic Capacitor Size Capacitance CL (inch code) L: 0.6 0.03 6.2 0.25 tolerance Rated Voltage 25 V Thickness 0.3 0.03 mm mm 0.3 W: 0.03 mm Inner electrode Cu Termination Cu Plating Sn 100% (Pb Free) Product Normal Special Reserved for future use Packaging Cardboard Type, 7" reel B. Samsung Reliablility Test and Judgement condition Performance Within specified tolerance Test condition 110% 0.5~5Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (x10) 300% of the rated voltage Voltage mechanical breakdown Temperature C0G Characterisitcs Adhesive Strength (From -55 to 125, Capacitance change shoud be within 30PPM/) No peeling shall be occur on the 200gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. Solderability within 5% or 0.5 whichever is larger More than 75% of terminal surface Capacitance 524 min Q Insulation is to be soldered newly 1) Sn63Pb37 solder 2355, 50.5sec. 2) SnAg3.0Cu0.5 solder 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec. Solder pot : 2705, 101sec. Performance Test condition Vibration Test Capacitance change : Humidity within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours x 3 direction (x, y, z) Capacitance change : 402, 90~95%RH, 500+12/-0hrs Amplitude : 1.5mm within 5% or 0.5 whichever is larger Q: 262 min IR : 1000Mohm or 50Mohm Whichever is Smaller Moisture Capacitance change : Resistance within 7.5% or 0.75 whichever is larger 402, 90~95%RH, 500+12/-0hrs Q: 120.67 min IR : With rated voltage 500Mohm or 25Mohm Whichever is Smaller High Temperature Capacitance change : With 200% Resistance within 3% or 0.3 whichever is larger Q: 262 min Max. operating temperature IR : of the rated voltage 1000+48/-0hrs 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : 1 cycle condition Cycling within 2.5% or 0.25 whichever is larger Min. operating temperature 25 Tan , IR : initial spec. Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.