Technical Data Sheet Product 222 Worldwide Version, October 1995 TYPICAL APPLICATIONS Prevents loosening through vibration and leakage of threaded fasteners. Particularly suitable for applications such as adjustment of set screws, small diameter or long engagement length fasteners where easy disassembly is required without shearing the screw. 135 >93 90 to 180 m hro Dic ate 50 25 l tee sS s e inl Sta s as Br 0 5min 10min 30min 1hr 3hr 6hr 5m m 30min 1hr 3hr 6hr 24hr 72hr Cure speed vs. temperature The rate of cure will depend on the ambient temperature. Graph below shows the breakaway strength developed with time at different temperatures on M10 steel nuts and bolts and tested according to ISO 10964. 24hr 72hr Cure Time, Hours Cure speed vs. bond gap The rate of cure will depend on the bondline gap. Gaps in threaded fasteners depend on thread type, quality and size. The following graph shows shear strength developed with time on steel pins and collars at different controlled gaps and tested according to ISO 10123. 75 50 25 0 5min10min 30min 1hr 3hr 24hr 72hr 6hr Cure Time, Hours Cure speed vs. activator Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph below shows breakaway strength developed with time using ACTIVATOR N and T on M10 Zinc Dichromate steel nuts & bolts and tested according to ISO 10964. % of Full Strength on Steel % of Full Strength on Steel Cure speed vs. substrate The rate of cure will depend on substrate used. The graph below shows the breakaway strength developed with time on M10 steel nuts and bolts compared to different materials and tested according to ISO 10964. c Zin 5min 10min 5 C 2,500 to 7,500 800 to 1,600 75 0 100 5,000 1200 l ee St 25 Cure Time, Hours TYPICAL CURING PERFORMANCE 100 50 m 5m 0.2 22 C Specific Gravity @ 25C Viscosity @ 25C, mPa.s (cP) Brookfield RVF Spindle 3 @ 2 rpm @ 20 rpm DIN 54453, MV D = 277 s-1 after t=180secs Flash Point (TCC), C Range 75 40 C Chemical Type Appearance Typical Value Dimethacrylate ester Opaque Purple, Fluorescent Liquid 1.05 m 5m 0.1 % of Full Strength on Steel PROPERTIES OF UNCURED MATERIAL 100 0.0 % of Full Strength on Steel PRODUCT DESCRIPTION LOCTITE(R) Product 222 is a single component anaerobic threadlocking material, which is thixotropic and develops low strength for easy disassembly. The product cures when confined in the absence of air between close fitting metal surfaces. 100 or at tiv c A No 75 t T Ac 50 tN Ac 25 0 5min10min 30min 1hr 3hr 6hr 24hr 72hr Cure Time, Hours TYPICAL PROPERTIES OF CURED MATERIAL Physical Properties Coefficient of thermal expansion, ASTM D696, K-1 Coefficient of thermal conductivity, ASTM C177, W.m-1 K- 80 x10-6 0.1 Specific Heat , kJ.kg-1 K-1 0.3 1 NOT FOR PRODUCT SPECIFICATIONS. THE TECHNICAL DATA CONTAINED HEREIN ARE INTENDED AS REFERENCE ONLY. PLEASE CONTACT LOCTITE CORPORATION QUALITY DEPARTMENT FOR ASSISTANCE AND RECOMMENDATIONS ON SPECIFICATIONS FOR THIS PRODUCT. ROCKY HILL, CT FAX: +1 (860)-571-5473 DUBLIN, IRELAND FAX: +353-(1)-451 - 9959 TDS 222, October 1995 PERFORMANCE OF CURED MATERIAL For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS). (After 24 hr at 22C on M10 steel nuts & bolts) Typical Value 6 (53) 4 (30) 14 (120) 14 (120) Breakaway Torque, ISO 10964, N.m (lb.in) Prevail Torque, ISO 10964, N.m (lb.in) Breakloose Torque, DIN 54454, N.m (lb.in) Max. Prevail Torque, DIN 54454, N.m (lb.in) Range 3 to 9 (25 to 80) 1 to 6 (10 to 50) 8 to 20 (71 to 180) 8 to 20 (71 to 180) Where aqueous washing systems are used to clean the surfaces before bonding, it is important to check for compatibility of the washing solution with the adhesive. In some cases these aqueous washes can affect the cure and performance of the adhesive. This product is not normally recommended for use on plastics (particularly thermoplastic materials where stress cracking of the plastic could result). Users are recommended to confirm compatibility of the product with such substrates. TYPICAL ENVIRONMENTAL RESISTANCE Test Procedure : Breakloose Torque, DIN 54454 Substrate: M10 Zinc Phosphate Nuts & Bolts Cure procedure: 1 week at 22C Directions for use For best performance surfaces should be clean and free of grease. Product should be applied to the bolt in sufficient quantity to fill all engaged threads. This product performs best in thin bond gaps, (0.05mm). Very large thread sizes may create large gaps which will affect cure speed and strength. This product is designed to give controlled friction, (torque/tension ratio), during assembly. In critical tightening applications this ratio should be confirmed. Hot Strength Tested at temperature. % RT Strength 100 75 Storage Product shall be ideally stored in a cool, dry location in unopened containers at a temperature between 8C to 28C (46F to 82F) unless otherwise labelled. Optimal storage is at the lower half of this temperature range. To prevent contamination of unused product, do not return any material to its original container. For further specific shelf life information, contact your local Technical Service Centre. 50 25 0 0 50 100 150 Temperature, C Data Ranges The data contained herein may be reported as a typical value and/or range (based on the mean value 2 standard deviations). Values are based on actual test data and are verified on a periodic basis. Heat Aging Aged at temperature indicated and tested at 22C. % Initial Strength at RT 125 100 120C 75 50 150C 25 0 0 1,000 2,000 3,000 4,000 5,000 Hours Chemical / Solvent Resistance Aged under conditions indicated and tested at 22C. Solvent Temp . % Initial Strength retained at 100 hr Motor Oil Leaded Petrol Brake Fluid Water/Glycol (50%/50%) Ethanol Acetone 500 hr 1000 hr 5000 hr 125 C 22C 22C 87C 100 95 90 85 95 95 80 95 95 80 95 95 80 95 90 80 22C 22C 95 100 95 90 90 90 90 90 Note The data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtained by others over whose methods we have no control. It is the user's responsibility to determine suitability for the user's purpose of any production methods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of persons against any hazards that may be involved in the handling and use thereof. In light of the foregoing, Loctite Corporation specifically disclaims all warranties expressed or implied, including warranties of merchantability or fitness for a particular purpose, arising from sale or use of Loctite Corporation's products. Loctite Corporation specifically disclaims any liability for consequential or incidental damages of any kind, including lost profits. The discussion herein of various processes or compositions is not to be interpreted as representation that they are free from domination of patents owned by others or as a license under any Loctite Corporation patents that may cover such processes or compositions. We recommend that each prospective user test his proposed application before repetitive use, using this data as a guide. This product may be covered by one or more United States or foreign patents or patent applications. GENERAL INFORMATION This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidising materials. Loctite is a Registered Trademark of Loctite Corporation, Hartford, CT 06106