AlteraTM MicroFit Heat - Shrinkable Tubing This specification covers the requirements for two types of single wall, electrical insulating, extruded tubing whose diameters will reduce to a predetermined size upon application of heat in excess of 175 C (347 F) for MT1000 and 140 C (284 F) for MT2000. The tubing shall be homogenous and essentially free from flaws, defects, pinholes, seams, cracks or inclusions. The tubing is fabricated from materials, which meet the requirements of U.S. Pharmacopeia Class VI Plastics. Color shall be translucent or black unless otherwise specified. Table 1: Dimensions inches (mm) As Supplied Expanded I.D. Minimum (D) MFT-*- No.1-** .014 (.356) MFT-*- No.2-** .024 (.610) MFT-*- No.33-** .045 (1.143) MFT-*- No.65-** .025 (.635) * = material MT1000 or MT2000 ** = color MT1000 is semi-rigid polyvinylidene material. MT2000 is medical grade polyolefin material. Size Recovered Recovered I.D. Recovered Wall Maximum (d) Maximum (W) .007 (.178) .005 (.127) .012 (.305) .006 (.152) .017 (.432) .007 (.118) .010 (.254) .013 (.330) Specification Control Drawing Tyco Electronics Corporation 300 Constitutional Drive Menlo Park, CA 94025 USA Title: Tyco Electronics reserves the right to amend this drawing at any time. Users should evaluate the suitability of the product for their application Cage Code: Scale: Size: 06090 None A AlteraTM MicroFit Heat - Shrinkable Tubing Document No : Altera MicroFit Rev. Date: Rev.: Sheet: 17-Sept-01 B 1 of 2 If this document is printed it becomes uncontrolled. Check for the latest revision. MT1000 Property Physical * Dimensions Tensile Strength Ultimate Elongation Secant Modulus (as supplied) Electrical Dielectric Strength Dielectric Withstand 3000V, 60 Hz Heavy Metals Analysis Cadmium Mercury Lead Bismuth Antimony Unit Requirement Test Method Inches (mm) PSI (MPa) Percent PSI (MPa) In accordance with Table 1 5000 minimum (34.5) 150 minimum 1x105 minimum (690) ASTM D 2671 ASTM D 2671, 2"/ minute ASTM D 2671 Volts/mil Volts/mm 800 minimum (31,500) ASTM D 2671 sec ppm 60 minimum 1 maximum (total of all metals) ASTM D 2671 USP XXII Physicochemical Tests-Plastics (Note 1) Unit Requirement Test Method Inches (mm) PSI (MPa) Percent PSI (MPa) In accordance with Table 1 3000 minimum (20.7) 200 minimum 5x104 minimum (344) ASTM D 2671 ASTM D 2671, 2"/ minute ASTM D 2671 Volts/mil Volts/mm 1000 minimum (39,360) ASTM D 2671 sec ppm 60 minimum 1 maximum (total of all metals) ASTM D 2671 USP XXII Physicochemical Tests-Plastics (Note 1) MT2000 Property Physical * Dimensions * Tensile Strength * Ultimate Elongation Secant Modulus (as supplied) Electrical Dielectric Strength Dielectric Withstand 3000V, 60 Hz Heavy Metals Analysis Cadmium Mercury Lead Bismuth Antimony * Denotes lot acceptance test Note 1: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitative analytical method. Rev. Date: 17-Sept-01 Rev.: Document No. Sheet: B Altera MicroFit 2 of 2 If this document is printed it becomes uncontrolled. Check for the latest revision.