SPECIFICATION CONTROL DRAWING 44A0111 TITLE WIRE, ELECTRIC, RADIATION-CROSSLINKED, TIN-COATED COPPER, Date o4MARA1 Revision P4 LIGHTWEIGHT, GENERALPURPOSE, 600 VOLT This specification sheet forms a part of the latest issue of Raychem Specification 44 and MIL-W-81044 as applicable. CONDUCTOR-TIN-COATEDCOPPER PRIMARY INSULATON - RADIATION-GROSSLINKED, EXTRUDED POLYALKENE JACKET- RADIATION-CROSSLINKED MODIFIED PVF2 Thickness: .003 + .001 in. TABLE |. CONSTRUCTION DETAILS DIAMETER OF FINISHED WIRE PART NUMBER | size | srRaNDING CONDUCTOR RESISTANCE | piAMETER rane uv (AWG) | (number x AWG) (m.) ane in.) | ibsit000 tt.) MINIMUM [MAXIMUM _[conms/1000 ft) 44A0111-26-" 26 10 x 38 018 021 413 034 +002 14 44A0111-242 24 19 x 36 023 026 26.2 040 + 002 20 44A0111-22 22 19 x 34 029 033 16.2 047 + 002 3.0 44A0111-20- 20 19x 32 037 041 0.88 055 +002 45 44A0111-18> 78 1 x 30 046 051 B23 055 4002 8 44A0111-16- 16 19x 29 052 058 781 O72 4003 6 44A0111-14 14 19 x 27 065 073 3.06 089 + 004 13.2 44A0111-120 12 37 x 28 084 090 2.02 108 +004 20.2 44A0111-10 10 37 _x 26 106 114 1.26 129 4.004 31.1 PART NUMBER WV 44A0111-24-" 4440111-18-* * * 4440111-12-* LIFECYCLE AND ACCELERATEDAGING TABLE II. PERFORMANCE DETAILS BEND TESTING MANDREL DIAMETER (inch) (+ 3%) IMMERSION, COLD BEND 500 200 750 WEIGHT (Ib) IMMERSION, LIFE CYCLEAND ACCELERATEDAGING 375 (+ 3%) . Users should evaluate the suitability of this product for their application. Specifications are subject to change without TE Connectivity also reserves the right to make changes in materials or processing, which do not affect compliance with any specification, without notification to Buyer. 1/ COLORS AND COLOR CODE DESIGNATORS SHALL BE IN ACCORDANCE WITH MIL-STD-681. OTHER CODES AND SUFFIXES MAY BE ADDED TO THE PART NUMBER. AS NECESSARY, TO CAPTURE ANY ADDITIONAL REQUIREMENTS IMPOSED BY THE PURCHASE ORDER. TE DIMENSIONS ARE ININCHES, AND UNLESS OTHERWISE DESIGNATED ARE NOMINAL. TE CONNECTIVITY Page 1 of 2 THIS SPECIFICATION SHEET TAKES PRECEDENCE OVER DOCUMENTS REFERENCED HEREIN. REFERENCED DOCUMENTS SHALL BE OF THE ISSUE IN EFFECT ON DATE OF INVITATION FOR BID. TE ConnectivityWire & Cable Of Oakside Avenue Redwood City, CA 94063-3600 Phone: 1-800-227-8816 Fax. 1-650-361-6297TE CONNECTIVITY SCD Number SPECIFICATION CONTROL DRAWING Page 2 of 2 44A0111 WIRE RATINGS AND ADDITIONAL REQUIREMENTS TEMPERATURE RATING: 150C, Maximum continuous conductortemperature VOLTAGE RATING: 600 volts (rms) at sea level ACCELERATED AGING: 300+ 2C for 6 hours Identification legibility, 225+ 2C for 6 hours BLOCKING: 150+ 2C for 24 hours COLOR: white preferred FLAMMABILITY: 30 seconds (maximum); 3 in. (maximum); no flaming of facial tissue HUMIDITY RESISTANCE: Insulation Resistance, 5000 Megonmms for 1000 ft. (minimum) IDENTIFICATION, STRIPING, ORBAND DURABILITY: 125 cycles (250 strokes) (minimum), 500 g weight IMMERSION: Diameter increase 5% (maximum); nocracking,no dielectric breakdown INSULATION ELONGATION AND TENSILE STRENGTH: Primary Insulation, Tensile Strength, 2500 Ibf/in? (minimum) Elongation, 150% (minimum) INSULATION FLAWS: Primary Insulation, Spark test, 1.5 kV (rms), at 60 Hz High Frequency Spark Test: 4.2 kV (rms) at 3.0 kHz Impulse Dielectric test, 6.0 kV (peak) Finished Wire, High Frequency Spark Test: 5.7 kV (rms) at 3.0 kHz Impulse Dielectric test, 8.0 kV (peak) INSULATION RESISTANCE: 5000 Megohms for 1000 ft. (minimum) LIFE CYCLE: 200 +2C for 168 hours LOW TEMPERATURE-COLD BEND: -65+ 2C for 4 hours SHRINKAGE: 300 + 2C, 0.125 in. (maximum) in 12 in. SMOKE TEST: 200+ 2C. No visible smoke SOLDERABILITY (95% minimum coverage }: per MIL-STD-202, Method 208, except without steam-aging, Type RMA Flux SURFACE RESISTANCE: 500 Megohms-in. (minimum), both readings THERMAL SHOCK RESISTANCE: 150 + 2C, 0.060 in. (maximum) VOLTAGE WITHSTAND TEST (POST ENVIRONMENTAL): 2500 volts (rms), 60 Hz, 5 minutes WICKING: 2.25 in. (maximum) PART NUMBER: The "*"in the part numbers on page 1 shall be replaced by a color code designator. 1/Example: AWG 20, white: 44A0111-20-9 1/ See Footer section on page 1