Scotch-WeldTM
Epoxy Adhesive
DP110 Translucent and Gray
Technical Data March 2019
Product Description 3M Scotch-Weld Epoxy Adhesive DP110 Translucent and Gray are two-part
epoxy adhesives which combine a fast cure with flexibility.
Features Controlled flow 20 minute handling strength
Duo-Pak cartridge dispensing system Good adhesion to many plastics and metals
Typical Uncured
Physical Properties Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Product
3M Scotch-Weld
Epoxy Adhesive
DP110 Translucent
3M Scotch-Weld
Epoxy Adhesive
DP110 Gray
Viscosity @ 72°F (23°C),
Base
30,000 - 70,000
40,000 - 90,000
73°F (24°C) (CPS)
Accelerator
30,000 - 70,000
40,000 - 90,000
Base Resin
Base
Accelerator
Modified Epoxy
Amine
Modified Epoxy
Amine
Color
Base
Accelerator
Translucent White
Light Yellow
Whit
e
Black
Net Weight
Base
9.1 - 9.4
9.1 - 9.4
(Lbs./Gallon)
Accelerator
9.0 - 9.3
9.0 - 9.3
Mix Ratio
Volume
100 : 100
100 : 100
B : A
Weight
100 : 99
100 : 99
Worklife @ 73°F (24°C)
(minutes)
8 - 13
8 - 13
Typical Cured
Physical Properties Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Product
3M Scotch-Weld
Epoxy Adhesive
DP110 Translucent
Color
Yellow Translucent
Shore D Hardness (approx.)
40
Elongation (approx.)
40%
- 2 -
3M Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
Typical Cured
Thermal Properties
Typical Cured
Electrical Properties
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Product
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Translucent
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Gray
Thermal Conductivity
BTU/Hr/Ft2/°F/Ft.
.106 @ 113°F (45°C)
.104 @ 113°F (45°C)
Thermal Coefficient of Expansion
-58°F (-50°C) - 32°F (0°C)
-58°F (-50°C) - 166°F (110°C)
80 x 10-6
200 x 10-6
73 x 10-6
165 x 10-6
Glass Transition Temp.
55°F (13°C)
61°F (16°C)
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Product
3M Scotch-Weld
Epoxy Adhesive
DP110 Translucent
3M Scotch-Weld
Epoxy Adhesive
DP110 Gray
Dielectric Strength (volts/mil)
520
470
Volume Resistivity (ohms - cm)
4.5 x 1010
6.9 x 1010
Typical Adhesive
Performance
Characteristics
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
The following product performance data was obtained in the 3M laboratory under
the conditions specified. The following data show typical results obtained with
Scotch-Weld epoxy adhesive DP110 Translucent and Gray when applied to
properly prepared substrates and cured for 48 hours at 73°F (23°C) under 2 psi
pressure and tested according to the specifications indicated.
Note: All data developed after a 48 hour cure @ 75°F (24°C) under 2 psi pressure
unless noted otherwise.
A. Aluminum Overlap Shear
Overlap shear strength was measured on FPL etched 1 in. wide by 1/2 in. overlap
specimens. The bonds were made from 2 panels of 4 in. x 7 in. x .063 in., 2024 T3
clad aluminum bonded together and cut into 1 in. wide specimens. The separation
rate of the testing jaws was .1 in./minute. Tests similar to ASTM D-1002.
Test Temp
3M Scotch-Weld
Epoxy Adhesive
DP110 Translucent
3M Scotch-Weld
Epoxy Adhesive
DP110 Gray
-67°F (-55°C)
2500 psi
2700 psi
75°F (24°C)
2500 psi
3500 psi
160°F (71°C)
270 psi
270 psi
180°F (82°C)
200 psi
250 psi
- 3 -
3M Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
Typical Adhesive
Performance
Characteristics
(continued)
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
B. Aluminum T-Peel
T-Peel bonds were measured on 1 in. wide specimens cut from two FPL etched 8 in.
x 8 in. x .032 in., 2024 T3 clad aluminum panels bonded together. The separation
note of the testing jaws was 20 in./minute. Tests similar to ASTM D-1876.
Test Temp
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Translucent
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Gray
75°F (24°C)
20 piw
20 piw
C. Overlap shear on abraded metals, plastics, and rubber
Overlap shear strengths were measured on 1 in. wide 1/2 in. overlap specimens.
These bonds were made individually using 1 in. x 4 in. pieces of substrate.
The thickness of the substrates were: cold rolled, galvanized and stainless steel
0.056-0.062 in., copper 0.032 in., brass 0.036 in., rubbers 0.125 in., plastics
0.125 in. All surfaces were prepared by solvent wiping/abrading/solvent wiping.
The jaw separation rate used for testing was 0.1 in. per minute for metals, 2 in. per
minute for plastics, and 20 in. per minute for rubbers.
Substrate
Overlap Shear (psi) @ 75°F (24°C)
3M Scotch-Weld
Epoxy Adhesive
DP110 Translucent
3M Scotch-Weld
Epoxy Adhesive
DP110 Gray
Aluminum/Aluminum
1000
2300
Cold Rolled Steel/Cold Rolled Steel
1500
2500
Stainless Steel/Stainless Steel
1500
2450
Galvanized Steel/Galvanized Steel
1500
2600
Copper/Copper
1500
1750
Brass/Brass
1500
2450
Styrene Butadiene Rubber/Steel
80 - 100
80 - 100
Neoprene Rubber/Steel
40 - 60
40 - 60
ABS/ABS Plastic
500
680
PVC/PVC, Rigid
400
390
Polycarbonate/Polycarbonate
500
660
Acrylic/Acrylic
250
480
Fiber Reinforced Polyester/Fiber
Reinforced Polyester
1400*
1400*
*The substrate broke during the test instead of the bond.
- 4 -
Adhesive*
6mm Nozzle
gms/minute
10mm Nozzle
gms/minute
Scotch-Weld epoxy adhesive DP110 Gray
Scotch-Weld epoxy adhesive DP110 Gray 100°F (38°C)
8.3
14.0
31.5
50.3
Scotch-WeldTM
Epoxy Adhesives
DP110 Translucent and Gray
Environmental
Resistance Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
Overlap shear specimens were prepared on aluminum as above and exposed to the
environment conditions described below.
Environment
Overlap Shear (psi) @ 75°F (24°C)
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Translucent
3M™ Scotch-Weld™
Epoxy Adhesive
DP110 Gray
Etched
Abraded
Etched
Abraded
Initial
2500
1000
2500
2300
30 days tap water @ 75°F (24°C)
2300
1250
2300
1250
3 days, 160°F (71°C), 100% rel. humidity
1200
700
1200
700
14 days in 5% salt spray @ 95°F (35°C)
500
150
500
150
Note: Avoid using either Scotch-Weld epoxy adhesive DP110 Translucent or Gray on metals
where the bonded parts will experience high humidity/hot water conditions. User must test
thoroughly adhesive performance for any environments which will be encountered.
3M EPX
Pneumatic Applicator
Delivery Rates
400 ml Applicator Maximum Pressure 73 psi
200 ml Applicator Maximum Pressure 58 psi
Scotch-Weld epoxy adhesive DP110 Gray
6.6
25.6
Scotch-Weld epoxy adhesive DP110 Gray 100°F (38°C)
35.1
115.9
Scotch-Weld epoxy adhesive DP110 Gray 125°F (49°C)
53.8
129.6
Scotch-Weld epoxy adhesive DP110 Gray 150°F (66°C)
332.0
687.0**
48.5/50 ml Applicator Maximum Pressure 50 psi
Adhesive*
1/4 in. Nozzle
gms/minute
Scotch-Weld epoxy adhesive DP110 Translucent
Scotch-Weld epoxy adhesive DP110 Gray
6.3
6.2 (nozzle cut back 2 divisions)
12.3
12.1 (nozzle cut back 2 divisions)
*Tests were run at a temperature of 70°F ± 2°F (21°C ± 1°C) and at maximum applicator pressure.
**Did not mix adequately.
3M Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
- 5 -
Handling/Curing
Information Directions for Use
1. For high strength structural bonds, paint, oxide films, oils, dust, mold release
agents and all other surface contaminants must be completely removed from
substrates to be bonded. However, the amount of surface preparation necessary
directly depends on the users required bond strength, environmental aging
resistance and economic practicalities. For specific surface preparations on
common substrates, see the section on surface preparation.
2. These products consist of two parts.
Mixing
For Duo-Pak Cartridges
3M Scotch-Weld Epoxy Adhesive DP110 Translucent and Gray are
supplied in a dual syringe plastic duo-pak cartridge as part of the 3M EPX™
Applicator system. To use, simply insert the duo-pak cartridge into the EPX
applicator and start the plunger into the cylinders using light pressure on the
trigger. Next, remove the duo-pak cartridge cap and expel a small amount of
adhesive to be sure both sides of the duo-pak cartridge are flowing evenly and
freely. If automatic mixing of Part A and Part B is desired, attach the EPX
mixing nozzle to the duo-pak cartridge and begin dispensing the adhesive. For
hand mixing, expel the desired amount of adhesive and mix thoroughly. Mix
approximately 15 seconds after a uniform color is obtained.
For Bulk Containers
Mix thoroughly by weight or volume in the proportions specified on the product
label or in the uncured properties section. Mix approximately 15 seconds after a
uniform color is obtained.
3. For maximum bond strength apply product evenly to both surfaces to be joined.
4. Application to the substrates should be made within 8 minutes. Larger quantities
and/or higher temperatures will reduce this working time.
5. Join the adhesive coated surfaces and allow to cure at 60°F (1C) or above until
completely firm. Heat up to 200°F (93°C), will speed curing. These products will
fully cure in 48 hours @ 75°F (24°C).
6. Keep parts from moving during cure. Contact pressure necessary. Maximum shear
strength is obtained with a 3-5 mil bond line.
7. Excess uncured adhesive can be cleaned up with ketone type solvents.*
*Note: When using solvents, extinguish all ignition sources, including pilot lights,
and follow the manufacturers precautions and directions for use.
Adhesive Coverage: A 0.005 in. thick bondline will typically yield a coverage of
320 sq. ft./gallon.
- 6 -
3M Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
Application Equipment
Suggestions These products may be applied by spatula, trowel or flow equipment.
Two part mixing/proportioning/dispensing equipment is available for intermittent or
production line use. These systems are ideal because of their variable shot size and
flow rate characteristics and are adaptable to many applications.
Surface Preparation For high strength structural bonds, paint, oxide films, oils, dust, mold release agents
and all other surface contaminants must be completely removed from substrate to be
bonded. However, the amount of surface preparation necessary directly depends on
the users required bond strength, environmental aging resistance and economic
practicalities.
The following cleaning methods are suggested for common surfaces:
Steel:
1. Wipe free of dust with oil-free solvent such as acetone or isopropyl alcohol
solvents.*
2. Sandblast or abrade using clean fine grit abrasives.
3. Wipe again with solvent to remove loose particles.*
4. If a primer is used, it should be applied within 4 hours after surface preparation.
Aluminum:
1. Alkaline Degrease: Oakite 164 solution (9-11 oz./gallon water) at 190°F ± 10°F
(88°C ± 23°C) for 10-20 minutes. Rinse immediately in large quantities of cold
running water.
2. Acid Etch: Place panels in the following solution for 10 minutes at 150°F ± 5°F
(66°C ± 23°C).
Sodium Dichromate 4.1 - 4.9 oz./gallon
Sulfuric Acid, 66°Be 38.5 o 41.5 oz./gallon
2024-T3 aluminum (dissolved) 0.2 oz./gallon minimum
Tap water as needed to balance
3. Rinse: Rinse panels in clear running tap water.
4. Dry: Air dry 15 minutes; force dry 10 minutes at 150°F ± 1F (6C ± 23°C).
5. If primer is to be used, it should be applied within 4 hours after surface preparation.
Plastics/Rubber:
1. Wipe with isopropyl alcohol.*
2. Abrade using fine grit abrasives.
3. Wipe with isopropyl alcohol.*
*Note: When using solvents, extinguish all ignition sources, including pilot lights,
and follow the manufacturers precautions and directions for use.
3M Scotch-Weld
Epoxy Adhesives
DP110 Translucent and Gray
- 7 -
Storage Store products at 60-80°F (16-27°C) for maximum storage life.
Shelf Life These products have a shelf life of 24 months in their unopened original
containers from date of manufacture.
Precautionary
Information
Refer to Product Label and Material Safety Data Sheet for health and safety information before using this
product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501.
Technical Information The technical information, guidance, and other statements contained in this document or otherwise
provided by 3M are based upon records, tests, or experience that 3M believes to be reliable, but the
accuracy, completeness, and representative nature of such information is not guaranteed. Such
information is intended for people with knowledge and technical skills sufficient to assess and apply
their own informed judgment to the information. No license under any 3M or third party intellectual
property rights is granted or implied with this information.
Product
Selection
and Use
Many factors beyond 3M’s control and uniquely within user’s knowledge and
control can affect the use and performance of a 3M product in a particular
application. As a result, customer is solely responsible for evaluating the product
and determining whether it is appropriate and suitable for customer’s
application, including conducting a workplace hazard assessment and reviewing
all applicable regulations and standards (e.g., OSHA, ANSI, etc.). Failure to
properly evaluate, select, and use a 3M product and appropriate safety products,
or to meet all applicable safety regulations, may result in injury, sickness, death,
and/or harm to property.
Warranty,
Limited Remedy,
and Disclaimer
Unless a different warranty is specifically stated on the applicable 3M product packaging or product
literature (in which case such warranty governs), 3M warrants that each 3M product meets the
applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER
WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO,
ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY, FITNESS FOR A
PARTICULAR PURPOSE, OR ARISING OUT OF A COURSE OF DEALING, CUSTOM, OR USAGE
OF TRADE. If a 3M product does not conform to this warranty, then the sole and exclusive remedy is,
at 3M’s option, replacement of the 3M product or refund of the purchase price.
Limitation of Liability Except for the limited remedy stated above, and except to the extent prohibited by law, 3M will not be
liable for any loss or damage arising from or related to the 3M product, whether direct, indirect, special,
incidental, or consequential (including, but not limited to, lost profits or business opportunity), regardless
of the legal or equitable theory asserted, including, but not limited to, warranty, contract, negligence, or
strict liability.
ISO 9001: 2000
This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001: 2000 standards
Industrial Adhesives and Tapes Division
3M Center, Building 225-3S-06
St. Paul, MN 55144-1000
800-362-3550 • 877-369-2923 (Fax)
www.3M.com/structuraladhesives
3M and Scotch-Weld are trademarks
of 3M Company.
©3M 2009 78-6900-2827-5