SPECIFICATION * Supplier : Samsung electro-mechanics * Product : Multi-layer Ceramic Capacitor (Reference sheet) CL42B102KJFNNNE CAP, 1nF, 2000V, 10%, X7R, 1808 * Samsung P/N : * Description : A. Samsung Part Number CL Series Size Dielectric Capacitance Capacitance tolerance Rated Voltage Thickness 42 B 102 K J F N N Samsung Multi-layer Ceramic Capacitor 1808 (inch code) L : 4.50 0.40 2000 V 1.25 0.20 E W : 2.00 0.20 Inner electrode Termination Plating Product Special Packaging X7R 1 nF 10 % N Ni Cu Sn 100% (Pb Free) Normal Reserved for future use Embossed Type, 7" reel B. Structure & Dimension Dimension() Samsung P/N CL42B102KJFNNNE L W T BW 4.50 0.40 2.00 0.20 1.25 0.20 0.80 0.30 C. Samsung Reliablility Test and Judgement Condition Judgement Capacitance Tan (DF) Insulation Resistance Appearance Withstanding Voltage Temperature Characteristics Adhesive Strength of Termination Bending Strength Solderability Within specified tolerance 0.025 max. Test condition 1 10% / 1.00.2Vrms *A capacitor prior to measuring the capacitance is heat treated at 150+0/-10 for 1hour and maintained in ambient air for 242 hours. 50050 Vdc 605 sec. 10,000Mohm or 500Mohmx Whichever is smaller No abnormal exterior appearance Microscope (x10) 120% of the rated voltage No dielectric breakdown or mechanical breakdown X7R (From -55 to 125, Capacitance change should be within 15%) No peeling shall be occur on the 500g*f, for 101 sec. terminal electrode Capacitance change : within 12.5% Bending to the limit (1) with 1.0mm/sec. More than 95% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Soldering Heat Vibration Test High Temperature Resistance Temperature Cycling Capacitance change : Tan , IR : initial spec. Capacitance change : Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. within 5% Amplitude : 1.5mm Capacitance change : within 12.5% Tan : 0.05 max IR : 1,000Mohm or 50Mohm x Whichever is smaller Capacitance change : within 7.5% Tan , IR : initial spec. From 10 to 55 (return : 1min.) 2hours x 3 direction (x, y, z) With 100% of the rated voltage Max. operating temperature 1,000+48/-0hrs 1 cycle condition Min. operating temperature Max. operating temperature 5 cycle test The reliability test condition can be replaced by the corresponding accelerated test condition. D. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 250, 6 sec max. ) Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers. 25 25 The products listed in this Specification sheet are NOT designed and manufactured for any use and applications set forth below. Please note that any misuse of the products deviating from products specifications or information provided in this Spec sheet may cause serious property damages or personal injury. We will NOT be liable for any damages resulting from any misuse of the products, specifically including using the products for high reliability applications as listed below. If you have any questions regarding this 'Limitation of Use and Application', you should first contact our sales personnel or application engineers. Aerospace/Aviation equipment Automotive or Transportation equipment (vehicles, trains, ships, etc) Medical equipment Military equipment Disaster prevention/crime prevention equipment Power plant control equipment Atomic energy-related equipment Undersea equipment Traffic signal equipment Data-processing equipment Electric heating apparatus, burning equipment Safety equipment Any other applications with the same as or similar complexity or reliability to the applications