SPECIFICATION CONTROL DRAWING 55A0114 Date WIRE, RADIATION-CROSSLINKED, MODIFIED, ETFE-INSULATED, SILVER-COATED HIGH STRENGTH COPPER ALLOY, LIGHTWEIGHT TITLE 06-21-04 Revision P This specification sheet forms a part of the latest issue of Raychem Specification 55A. CONDUCTOR - INSULATON - SILVER-COATED HIGH STRENGTH COPPER ALLOY RADIATION-CROSSLINKED, MODIFIED ETFE TABLE I. CONSTRUCTION DETAILS PART NUMBER 1/ 55A0114-30-* 55A0114-28-* 55A0114-26-* 55A0114-24-* 55A0114-22-* 55A0114-20-* 55A0114-18-* 55A0114-16-* WIRE CONDUCTOR SIZE STRANDING (AWG) (number x AWG) 30 28 26 24 22 20 18 16 7 7 19 19 19 19 19 19 x x x x x x x x DIAMETER OF STRANDED CONDUCTOR (in.) MINIMUM .011 .014 .018 .023 .029 .037 .046 .052 38 36 38 36 34 32 30 29 FINISHED WIRE MAXIMUM MAXIMUM RESISTANCE AT 20C (ohms/1000 ft.) .012 .016 .020 .025 .031 .039 .050 .057 117.4 74.4 44.8 28.4 17.5 10.7 6.8 5.3 DIAMETER (in.) .024 .027 .032 .037 .043 .050 .060 .068 MAXIMUM WEIGHT (lbs/1000 ft.) .002 .002 .002 .002 .002 .002 .002 .002 .66 .91 1.4 2.0 2.9 4.4 6.5 8.3 TABLE II. PERFORMANCE DETAILS BEND TESTING PART NUMBER 1/ 55A0114-30-* 55A0114-28-* 55A0114-26-* 55A0114-24-* 55A0114-22-* 55A0114-20-* 55A0114-18-* 55A0114-16-* WEIGHT (lb) ( 3%) MANDREL DIAMETER (inch) ( 3%) IMMERSION, LIFE CYCLE AND ACCELERATED AGING .250 .250 .375 .375 .500 .500 .500 .750 COLD BEND IMMERSION, LIFE CYCLE AND ACCELERATED AGING .375 .375 .500 .500 .750 .750 1.00 1.00 .125 .125 .125 .250 .375 .500 .500 .750 COLD BEND .500 .500 .500 1.00 1.00 1.00 1.00 1.00 Users should evaluate the suitability of this product for their application. Specifications are subject to change without notice. Tyco Electronics also reserves the right to make changes in materials or processing, which do not affect compliance with any specification, without notification to Buyer. 1/ COLORS AND COLOR CODE DESIGNATORS SHALL BE IN ACCORDANCE WITH MIL-STD-681. OTHER CODES AND SUFFIXES MAY BE ADDED TO THE PART NUMBER, AS NECESSARY, TO CAPTURE ANY ADDITIONAL REQUIREMENTS IMPOSED BY THE PURCHASE ORDER. DIMENSIONS ARE IN INCHES, AND UNLESS OTHERWISE DESIGNATED ARE NOMINAL. Page 1 of 2 THIS SPECIFICATION SHEET TAKES PRECEDENCE OVER DOCUMENTS REFERENCED HEREIN. REFERENCED DOCUMENTS SHALL BE OF THE ISSUE IN EFFECT ON DATE OF INVITATION FOR BID. R Wire & Cable 501 Oakside Avenue Redwood City, CA 94063-3800 Phone: 1-800-227-8816 Fax: 1-650-361-6297 SCD Number SPECIFICATION CONTROL DRAWING Page 2 of 2 55A0114 WIRE RATINGS AND ADDITIONAL REQUIREMENTS TEMPERATURE RATING: 200C, Maximum continuous conductor temperature VOLTAGE RATING: 600 volts (rms) at sea level ACCELERATED AGING (CROSSLINKING PROOF): 300 3C for 7 hours BLOCKING: 230 3C for 24 hours COLOR: white preferred CONCENTRICITY: 70% (minimum) FLAMMABILITY: Procedure 1, 3 seconds (maximum); 3 in. (maximum); no flaming of facial tissue. HUMIDITY RESISTANCE: Insulation Resistance, 5000 megohms for 1000 ft. (minimum) IDENTIFICATION, COLOR STRIPING AND BAND DURABILITY: 125 cycles (250 strokes) (minimum), 500 g weight IMMERSION: Diameter increase 5% (maximum); no cracking, no dielectric breakdown INSULATION ELONGATION AND TENSILE STRENGTH: Elongation, 75% (minimum) Tensile strength, 5000 lbf/in (minimum) INSULATION FLAWS: Spark Test, 5.7 kV (rms) at 3 kHz Impulse DielectricTest, 8.0 kV (peak); INSULATION RESISTANCE: 5000 megohms for 1000 ft (minimum) INSULATION THICKNESS: 0.005 in. (minimum) LIFE CYCLE: 230 3C for 500 hours LOW TEMPERATURE-COLD BEND: -65 3C for 4 hours SHRINKAGE: 230 3C, for 6 hours, 0.125 in. (maximum) in 12 in. SOLDERABILITY: Per MIL-STD-202, Method 208, without steam aging SMOKE TEST: 250 5C. No visible smoke SURFACE RESISTANCE: 500 Megohms-in. (minimum), both readings THERMAL SHOCK RESISTANCE: 200 3C, 0.060 in. (maximum) VOLTAGE WITHSTAND TEST (Post Environmental): 2500 volts (rms), 60 Hz WRAP TEST: 313 3C for 2 hours PART NUMBER: The "*" in the part numbers on page 1 shall be replaced by a color code designator. 1/ Example: AWG 22, white: 55A0114-22-9 AWG 22, white with black stripe: 55A0114-22-90 1/ See footer section on page 1