3M™Dual Lock™R eclosable Fasteners
SJ3560(Type 250) • SJ3561 (Type 400) • SJ3562 (Type 170)
Typical System
Performance
Physical Pr operties
and Performance
Characteristics
Note: The following technical inf ormation and data is intended as a user guide r epresenting
typical performance and should not be used for specif ications.
Unless stated differently, typical performance characteristics were measured under controlled laboratory
conditions of 72°F (22°C) and 50% Relative Humidity to obtain maximum reliability. The user should
evaluate products in the actual application to ensure suitable performance for the intended use.
- 2 -
System Performance(a)
3M™ Dual Lock™ 3M™ Dual Lock™
Reclosable Fastener Reclosable Fastener 3M™ Scotchmate™
SJ3562 (Type 170) SJ3560 (Type 250) SJ3571 (loop)
engaged to engaged to engaged to
3M™ Dual Lock™ 3M™ Dual Lock™ 3M™ Dual Lock™
Reclosable Fastener Reclosable Fastener Reclosable Fastener
SJ3560 (Type 250) SJ3561 (Type 400) SJ3560 (Type 250)(b)
TENSILE (Rigid to Rigid Substrates) lbsF/sq inch (kNewtons/m2) @ 72°F/50% RH
Dynamic Tensile Engagement Strength 10 (69) 60 (414) <1 (<6.9)
Dynamic Tensile Disengagement(c) 23 (159) 107 (738) 29 (200)
Static Tensile Holding Power Holds minimum 2.2 #/in2(155 grams/cm2)
for indicated time and temperature
100°F/100% RH 10,000 minutes 10,000 minutes 10,000 minutes
200°F 10,000 minutes 10,000 minutes 10,000 minutes
220°F 10,000 minutes 10,000 minutes 10,000 minutes
250°F 3 minutes 3 minutes 300 minutes
SHEAR (Rigid to Rigid Substrates) lbsF/sq inch (kNewtons/m2)
Dynamic Shear (1" x 1" overlap)(c) 11 (76) 70 (483) 112 (772)
Static Shear Holding Power Holds minimum 2.2 #/in2(155 grams/cm2)
for indicated time and temperature
100°F/100% RH 7,200 minutes 10,000 minutes 10,000 minutes
200°F 20,000 minutes 20,000 minutes 20,000 minutes
220°F 20,000 minutes 20,000 minutes 20,000 minutes
250°F 3,500 minutes 3,500 minutes 3,500 minutes
PEEL AND CLEAVAGE(c) Pounds/inch width (grams/cm width)
Cleavage Strength (Rigid to Rigid) 8.3 (1485) 28.5 (5099) 12.4 (2218)
Peel Strength (“T” Peel, Flexible to Flexible) 0.5 (89) 1.7 (304) 2.7 (483)
Peel Strength (90° Peel, Flexible to Rigid) 1.6 (286) 5.4 (984) 4.1 (733)
ENGAGED THICKNESS(d) Inches (mm) ± Tolerance
(Nominal without liner) 0.21 (5.4) ± 15% 0.23 (5.9) ± 15% 0.20 (5.0)
CLOSURE CYCLE LIFE(e) 1,000 1,000 50
SHELF LIFE(f) 24 months 24 months 24 months
Note: Long Term Static Load: Conditions such as temperature variations, engagement area, closure pressure and vibrations or side to
side movement after engagement or prolonged periods of exposure to environmental factors can affect the closure strength and long term
static load performance. Fasteners may slip or creep in the direction of the static load forces when subjected to static loads at temperatures
or weights greater than indicated. The user is responsible for designing the amount of fastening area based upon the specific conditions for
the application. Four square inches of fastening area per pound of static load is suggested as a starting point for such evaluations.
a) The expected system perf ormance of 3M™ Dual Lock™ Reclosable Fasteners are in approximately the follo wing increasing order of
strength: Dual Lock SJ3562 engaged to Dual Lock SJ3560 < (less than) Dual Lock SJ3561 engaged to Dual Lock SJ3562 ≈(approximately
equal to) Dual Lock SJ3560 engaged to Dual Lock SJ3560 < Dual Lock SJ3560 engaged to Dual Lock SJ3561. The combinations of Dual
Lock SJ3561 engaged to Dual Lock SJ3561 and Dual Lock SJ3562 engaged to Dual Lock SJ3562 are not recommended.
b) Scotchmate loop engaged to Dual Lock provides increased strength over standard 3M™ Scotchmate™ Reclosable Fasteners. Due to this
increased strength, extra care should be given to ensure the maximum bond strength is obtained to the substrates being joined. Failure to
obtain bond strengths to the substrate that are sufficiently high may cause the fastener to release from the substrate upon disengagement.
c) Dual Lock SJ3560, SJ3561, SJ3562 and Scotchmate SJ3571 were engaged with firm pressure and disengaged at the rate of 12 inches
(305 mm) per minute.
d) Engaged thickness will decrease if a load is applied or increase if a separation force is applied.
e) Cycle Life is the number of cycles (openings and closings) that the fastener is subjected to while maintaining 50% or greater of the
original tensile values.
f) Shelf life is from date of manufacture when stored in original packaging at 72°F (22°C) and 50% relative humidity.