MCB0603STE141K - KOA Speer Electronics, Inc.

CERTIFIED

SS-219 R6

AHA 12/19/01

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 1 OF 8

Multi Layer Ferrite Chip Beads

Type MCB

■

Designed to reduce noise at high frequencies

■

Standard EIA Packages: 0402, 0603, 0805, 1206

■

Nickel barrier with solder overcoat for excellent solderability

■

Magnetically shielded

* Please note: KSE’s part

numbers do not contain

any spaces or hyphens.

MCB 0603 G TE 500 J

Type Size Material Packaging Impedance Tolerance

Permability TE: 7" Embossed Plastic 2 Significant Figure J:±5%

Code: T: 7" Paper Tape + 1 Multiplier K:±10%

F (0402 size only) Example: 500 = 50ΩM:±20%

G 0402: 10,000 pcs/reel P:±25%

S 0603: 4,000 pcs/reel

L 0805: 4,000 pcs/reel

P 1206: 3,000 pcs/reel

3. Ordering and Specifying Information*

Part

0603

0805

1206

2. 2.1 Dimensions

1. General

Table 1

0.063±0.006

(1.60±0.15)

0.079±0.008

(2.00±0.20)

0.049±0.008

(1.25±0.20)

0.035±0.008

(0.90±0.20)

0.020±0.010

(0.51±0.25)

0.126±0.008

(3.20±0.20)

0.063±0.008

(1.60±0.20)

0.043±0.008

(1.10±0.20)

0.020±0.010

(0.51±0.25)

0.031±0.006

(0.80±0.15)

0.031±0.006

(0.80±0.15)

0.014±0.006

(0.36±0.15)

LWHP

Dimensions - inches (mm)

Terminations

(metalization

bands)

0402

0603

0805

1206

Solder

Nickel

Silver

Metalization

Electrodes

KOA SPEER ELECTRONICS, INC.

0402 0.039±0.004

(1.00±0.10)

0.020±0.004

(0.50±0.10)

0.020±0.004

(0.50±0.10)

0.010±0.004

(0.25±0.10)

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 2 OF 8

SS-219 R6

4. Standard Applications

MCB0603GTE300* 30 0.1 400

MCB0603GTE400* 40 0.1 400

MCB0603GTE600* 60 0.2 300

MCB0603GTE750* 75 0.2 300

MCB0603GTE800* 80 0.2 300

MCB0603GTE900* 90 0.3 250

MCB0603GTE101* 100 0.3 250

MCB0603GTE121* 120 0.3 250

MCB0603GTE141* 140 0.3 250

MCB0603GTE151* 150 0.3 250

MCB0603GTE181* 180 0.3 250

MCB0603GTE221* 220 0.3 250

MCB0603GTE301* 300 0.35 230

MCB0603GTE421* 420 0.4 210

MCB0603GTE601* 600 0.45 210

MCB0603GTE102* 1,000 0.6 190

Impedance

@ 100MHz

Ω

Maximum DC

Resistance

Ω

Allowable

DC Current

(mA)

Operating

Temperature

-55°C

125°C

Ordering

Code

T: Paper Tape (0402 size only) TE: Embossed Plastic * Add Tolerance Character (J, K, M, P)

KOA SPEER ELECTRONICS, INC.

MCB0402GT100* 10 0.05 500

MCB0402GT150* 15 0.07 300

MCB0402GT700* 70 0.4 200

MCB0402GT121* 120 0.5 200

MCB0402GT221* 220 0.7 100

MCB0402GT601* 600 1.1 50

MCB0402GT102* 1000 1.5 50

MCB0603GTE152* 1,500 0.85 100

MCB0603GTE182* 1,800 0.95 50

MCB0603GTE202* 2,000 0.8 50

MCB0603STE180* 18 0.1 400

MCB0603STE121* 120 0.4 200

MCB0603STE141* 140 0.3 200

SS-219 R6

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 3 OF 8

4. Standard Applications (continued)

MCB0805GTE101* 100 0.15 400

MCB0805GTE121* 120 0.15 400

MCB0805GTE151* 150 0.3 200

MCB0805GTE181* 180 0.3 200

MCB0805GTE201* 200 0.3 200

MCB0805GTE301* 300 0.3 200

MCB0805GTE401* 400 0.3 200

MCB0805GTE421* 420 0.3 200

MCB0805GTE601* 600 0.3 200

MCB0805GTE751* 750 0.4 200

MCB0805GTE102* 1,000 0.4 200

TE: Embossed Plastic * Add Tolerance Character (J, K, M, P)

Impedance

@ 100MHz

Ω

Maximum DC

Resistance

Ω

Allowable

DC Current

(mA)

Operating

Temperature

-55°C

125°C

Ordering

Code

MCB0805FTE050* 5 0.07 800

MCB0805FTE070* 7 0.1 800

MCB0805FTE100* 10 0.1 800

MCB0805FTE110* 11 0.1 800

MCB0805FTE170* 17 0.1 800

MCB0805FTE300* 30 0.1 800

MCB0805FTE400* 40 0.1 800

MCB0805FTE500* 50 0.1 800

MCB0805FTE600* 60 0.1 800

MCB0805FTE750* 75 0.1 800

MCB0805FTE800* 80 0.15 400

MCB0805GTE900* 90 0.15 400

KOA SPEER ELECTRONICS, INC.

MCB0805GTE182* 1,800 0.8 200

MCB0805GTE152* 1,500 0.55 200

MCB0603STE421* 420 0.5 200

MCB0603STE601* 600 0.65 200

MCB0603STE721* 720 0.7 150

MCB0603STE102* 1,000 0.6 50

MCB1206STE181* 180 0.3 300

SS-219 R6

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 4 OF 8

KOA SPEER ELECTRONICS, INC.

4. Standard Applications (continued)

MCB1206FTE201* 200 0.3 300

MCB1206FTE301* 300 0.4 300

MCB1206FTE601* 600 0.5 200

MCB1206GTE102* 1,000 0.7 150

MCB1206GTE152* 1,500 @ 50MHz 0.9 100

Impedance

@ 100MHz

Ω

Maximum DC

Resistance

Ω

Allowable

DC Current

(mA)

Operating

Temperature

-55°C

125°C

Ordering

Code

MCB1206GTE202* 2,000 @ 30MHz 0.6 100

MCB1206FTE500* 50 0.1 600

MCB1206FTE600* 60 0.1 600

MCB1206FTE700* 70 0.1 200

MCB1206FTE800* 80 0.2 400

MCB1206FTE900* 90 0.2 400

MCB1206FTE101* 100 0.2 400

MCB1206FTE121* 120 0.2 400

MCB1206FTE190* 19 0.1 600

MCB1206FTE260* 26 0.1 600

MCB1206FTE300* 30 0.1 600

MCB1206FTE310* 31 0.1 600

MCB0805LTE601* 600 0.4 100

MCB0805GTE202* 2,000 0.7 200

MCB0805STE180* 18 0.1 600

MCB0805STE201* 200 0.4 200

MCB0805STE601* 600 0.4 200

MCB0805STE751* 750 0.7 200

MCB0805STE102* 1,000 0.75 100

MCB1206STE300* 30 0.1 600

MCB1206STE601* 600 0.3 200

TE: Embossed Plastic * Add Tolerance Character (J, K, M, P)

MCB1206FTE151* 150 0.15 300

MCB0805STE272* 2,700 0.8 200

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 5 OF 8

SS-219 R6

Item Requirement Conditions

Operating Temperature -55°C ~ +125°C

Storage Temperature 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be

used to reduce the potential of oxidation on

the terminations during storage.

Resistance to Solder Change in Impedance: Relative to value before Flux: 5-10 sec dip

Heat test ±20%. After Flux: Air dry for 15 sec

Appearance: There shall be no cracking Preheat: 150°C ±10°C

Solder Coverage: More than 75% of the terminal Preheat Time: 60 sec

electrode shall be covered with solder. Solder Temp: 260°C ±5°C

Dip Time: 10 ±1 sec

Solderability Solder Coverage: More than 95% of the Flux: 5-10 sec dip

termination shall be covered with solder. After Flux: Air dry for 15 sec

Solder Temp: 245°C ±5°C

Dip Time: 5 ±0.5 sec

Leach Resistance Appearance: There shall be no visible signs of The bead shall be subjected to the following

physical or mechanical damage (i.e. no cracks) 5 steps for the period of time shown below.

Terminations: Termination must not be leached The 5 steps constitute one (1) rotation.

away for more than 5%. 4 rotations shall be carried out.

1) Flux: 5-10 sec

2) After Flux: Air dry for 15 sec

3) Solder Temp: 230°C ±5°C

4) Dip Time: 5 ±0.5 sec

5) Cool: Air cool for 60 seconds

Insulation Resistance Insulation Resistance: Min 1G ohms

Solvent Resistance Change in Impedance: Relative to value before Cleaning by:

test ±10%. Washer: Ultrasonic washer (100W)

Solvent: Isopropyl alcohol

Time: 3 minutes

Terminal Strength Appearance: The terminal electrode shall not Type W(kgf) Time

(hanging test) break off, nor shall there be damage to the body. 0402 N/A

0603 0.5 30 sec ±2 sec

0805 1.0 30 sec ±2 sec

1206 1.5 30 sec ±2 sec

Terminal Strength Appearance: There shall be no evidence of Type W(kgf) Time

(push test) mechanical degradations to terminals or body. 0402 N/A

0603 1.4 60 sec

0805 1.8 60 sec

1206 2.3 60 sec

5. Characteristics

KOA SPEER ELECTRONICS, INC.

SS-219 R6

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 6 OF 8

KOA SPEER ELECTRONICS, INC.

Item Requirement Conditions

Bending Strength Appearance: There shall be no physical or Board: 90x40x1.6mm

mechanical damage Bend: 1mm

Impedance: Relative to initial value before test Time: 5 sec

±10%

Mechanical Shock Appearance: There shall be no physical or Force: 50G

mechanical damage Time: 11 msec

Impedance: Relative to initial value before test There shall be 3 shocks in each of 6 directions

±10% (18 shocks total).

Vibration Impedance: Relative to initial value ±10% Only endurance conditioning by sweeping shall

be made. The entire frequency range from

10-2,000Hz and return to 10Hz in 20

minutes (this shall constitute one cycle).

Amplitude: 1.5mm

The test shall have a 15G peak and shall be

applied for a period of 4 hours (12 cycles)

in each of 3 mutually perpendicular directions

(a total of 36 cycles within a total of 12 hours).

Thermal Shock Appearance: There shall be no physical or Step Temperature Time

mechanical damage. 1-start -40°C ±2°C

—

Impedance: Relative to initial value ±20%. 2-hold -40°C ±2°C 30 min ±5 min

DCR: The DCR shall not exceed initial specified 3-transfer

—

0.5 min max.

value. 4-hold +105°C ±2°C 30 min ±5 min

5-transfer

—

0.5 min max.

Testing of the parts will be made at 0 hours, 250

hours and 500 hours. Before testing the parts Steps 1 thru 5 constitute one complete cycle

shall be allowed to cool to room temperature for and the test shall consist of a total of 500

24 hours. cycles.

Load Humidity Appearance: There shall be no physical or Temperature: 85°C ±2°C

mechanical damage Relative Humidity: 85%

Impedance: Relative to initial value ±15% Time: 1,000 hours total

Apply: 100% rated current

Measurements shall be taken at 0 hours, 250

hours, 500 hours and 1,000 hours and shall meet

the conditions stated above.

Life Test Appearance: There shall be no physical or Temperature: 85°C ±2°C

mechanical damage Time: 1,000 hours total

Impedance: Relative to initial value ±15% Apply: 100% rated current

Measurements shall be taken at 0 hours, 250

hours, 500 hours and 1,000 hours and shall meet

the conditions stated above.

5. Characteristics (continued)

SS-219 R6

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

PAGE 7 OF 8

6. Packaging Specifications

KOA’s multilayer components are provided on tape-and-reel

for use in pick-and-place machines. The reel size is 7 inch.

7. Dimensions - inches (mm)

8. Chip Quantities Per Reel

0.043±0.002

(1.1±0.1)

0.075±0.002

(1.9±0.1)

0.043±0.002

(1.1±0.1)

0.063±0.002

(1.6±0.1)

0.093±0.002

(2.4±0.1)

0.046±0.002

(1.2±0.1)

0.071±0.002

(1.8±0.1)

0.138±0.002

(3.5±0.1)

0.048±0.002

(1.2±0.1)

0.079±0.004

(2.0±0.1)

0.069±0.004

(1.75±0.10)

0.138±0.002

(3.50±.005)

0.318±0.002

(8.1±0.1) 0.157±0.004

(4.0±0.1)

0.157±0.004

(4.0±0.1) 0.079±0.002

(2.00±0.05)

0.059±0.004

(1.5+0.1/-0.0) 0.039 min.

(1.0 min.)

0.009±0.001

(0.23±0.02)

1206

(3216)

0805

(2012)

0603

(1608)

0402

(1005)

0603

(1608)

0805

(2012)

1206

(3216)

Tape

EFWP

1Po P2D1tDo

Bo Ko

Parts on

7 inch (178mm) ReelChip Size

0603 (1608)

0805 (2012)

1206 (3216) 3,000

4,000

Po P2

D1P1

KOA SPEER ELECTRONICS, INC.

0.026±0.004

(0.65±0.1)

0.046±0.004

(1.17±0.1)

0.025±0.004

(0.63±0.1)

0402

(1005)

0402 (1005) 10,000

0.040±0.002

(1.0±0.05) N/A

KOA SPEER ELECTRONICS, INC.

SS-219 R6

Bolivar Drive

■

P.O. Box 547

■

Bradford, PA 16701

■

USA

■

814-362-5536

■

Fax 814-362-8883

■

www.koaspeer.com

Notice: The information contained in this Spec Sheet is believed to be accurate and up-to-date. KOA Speer Electronics reserves this right to change these specifications without notice.

PAGE 8 OF 8

10. Recommended Temperature Profiles for Soldering

250°C

150°C

60 Seconds Max.

Preheat 100

Seconds Max.

Soldering

10 Seconds Max.

Natural

Cooling

Recommended Temperature Profile

for Wave Soldering

250°C

150°C

60 Seconds Max.

Preheat 100

Seconds Max.

Soldering

10 Seconds Max.

Natural

Cooling

Recommended Temperature Profile

for Reflow Soldering

20 Seconds Max.

200°C

9. Recommended PC Board Land Patterns - mm (inches)

0603 (1608) 2.6 (0.102)

3.0 (0.118)

4.4 (0.173)

0.6 (0.023)

1.0 (0.039)

2.2 (0.087)

0.8 (0.031)

1.0 (0.039)

1.4 (0.055)

0805 (2012)

1206 (3216)

Chip Size L G H

0402 (1005) 1.3 (0.051) 0.4 (0.016) 0.5 (0.020)