DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS Class 2, Y5V Preliminary specification - Dec 26, 2005 V.11 16/25/50 V Phycomp Product specification Surface-mount ceramic multilayer capacitors FEATURES Class 2, Y5V 16/25/50 V QUICK REFERENCE DATA DESCRIPTION * Five standard sizes VALUE * High capacitance per unit volume Rated voltage UR (DC) 16 V, 25 V, 50 V * Supplied in tape on reel Capacitance range (E6 series) 10 nF to 10 F; note 1 * NiSn terminations. Tolerance on capacitance 20% (M); -20% to +80% (Z) Test voltage (DC) for 1 minute: 2.5 x UR Sectional specifications IEC 60384-10, second edition 1989-04 APPLICATIONS Detailed specification based on IEC 60384-10-1 * Consumer electronics, for example: End terminations NiSn Climatic category (IEC 60068) 30/85/21 - Tuners - Television receivers - Video recorders Note 1. Measured at 25 C, 1 V and 1 kHz, using a four-gauge method. - All types of cameras - Mobile telephones. terminations DESCRIPTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two terminations and finally covered with a layer of plated tin (NiSn). A cross section of the structure is shown in Fig.1. 2005 Dec 26 Rev.11 electrodes MLB457 ceramic material Fig.1 Construction of a ceramic multilayer capacitor. 2 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V MECHANICAL DATA W T L2 L4 L3 MBB211 L1 For dimensions see Table 1. Fig.2. Component outline. Physical dimensions Table 1 Capacitor dimensions; see Fig.2 L1 CASE SIZE W L2 and L3 . T MIN. MAX. MIN. MAX. L4 MIN. 0.45 0.55 0.15 0.30 0.40 Dimensions in millimetres 0402 1.0 0.05 0.5 0.05 0603 1.6 0.10 0.8 0.07 0.73 0.87 0.25 0.65 0.40 0805 2.0 0.10 1.25 0.10 0.50 1.35 0.25 0.75 0.55 1206 3.2 0.15 1.6 0.15 0.50 1.75 0.25 0.75 1.40 1210 3.2 0.20 2.5 0.20 1.40 1.60 0.25 0.75 1.40 Dimensions in inches 0402 0.040 0.002 0.020 0.002 0.018 0.022 0.008 0.012 0.016 0603 0.063 0.004 0.032 0.003 0.029 0.035 0.010 0.026 0.016 0805 0.079 0.004 0.049 0.004 0.020 0.053 0.010 0.030 0.022 1206 0.126 0.006 0.063 0.006 0.020 0.069 0.010 0.030 0.056 1210 0.126 0.008 0.098 0.008 0.047 0.069 0.010 0.030 0.056 2005 Dec 26 Rev.11 3 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V SELECTION CHART FOR 16 V AND 25 V C (nF) LAST TWO DIGITS OF 12NC 16 V 0402 0603 0805 25 V 1206 1210 0603 0805 1206 0.6 0.1 0.6 0.1 1 23 1.5 25 2.2 27 3.3 29 4.7 32 6.8 34 10 36 15 38 22 41 33 43 47 45 68 47 100 49 150 52 220 54 330 56 470 58 680 61 1,000 63 0.85 0.1 1.15 0.1 2,200 67 1.15 0.1 0.85 0.1 4,700 72 0.85 0.1 0.85 0.1 10,000 76 1.15 0.1 0.5 0.05 1210 0.8 0.07 0.8 0.07 0.85 0.1 0.85 0.1 0.85 0.1 1.5 0.1 1.15 0.1 1.5 0.1 Note 1. Values in shaded cells indicate thickness class in mm. 2005 Dec 26 Rev.11 4 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V SELECTION CHART FOR 50 V C (nF) LAST TWO DIGITS OF 12NC 10 05 15 06 22 07 33 08 47 09 68 11 100 12 150 13 220 14 330 15 470 16 680 17 1 000 18 50 V 0603 0805 0.8 0.07 0.6 0.1 1206 0.6 0.1 0.85 0.1 0.85 0.1 1.15 0.1 Note 1. Values in shaded cells indicate thickness class in mm. Thickness classification and packing quantities THICKNESS CLASSIFICATION (mm) 0.5 0.05 0.6 0.10 0.8 0.07 0.85 0.10 1.15 0.10 1.25 0.10 1.5 0.10 2005 Dec 26 Rev.11 8 mm TAPE WIDTH QUANTITY PER REEL 180 mm; 7" 330 mm; 13" PAPER BLISTER PAPER BLISTER 10 000 4 000 4 000 4 000 - - - - - - - 3 000 3 000 3 000 50 000 20 000 15 000 15 000 - - - - - - - 10 000 1 000 - 5 QUANTITY PER BULK CASE 0402 0603 0805 50 000 - - - - - - - - 15 000 15 000 - - - - 10 000 - 8 000 - 5 000 - www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V ORDERING INFORMATION Components may be ordered by using either a Phycomp's unique 12NC or simple 15-digit clear text code. Ordering code 12NC (preferred) 2 2 X X handbook, full pagewidth X X X X 9 X X X Carrier type 22 blister 38 paper 54 bulk Capacitance value(1) Rated voltage - Termination 78 16 V; NiSn 91 25 V; NiSn 58 50 V; NiSn Tolerance 7 20% 8 -20/+80% Size 7 0402 6 0603 0 0805 1 1206 2 1210 CCA620_a Packaging(2) 1 reel: 180 mm; 7" 5 reel: 330 mm; 13" 4 bulk case (1) Refer to chapters "Selection chart for 16 V and 25 V" and "Selection chart for 50 V". (2) Quantity on reel depends on thickness classification, see section "Thickness classification and packing quantities". Phycomp Clear text code EXAMPLE: 12062F105M8BB0D Size Code 0402 0603 0805 1206 1210 Temp. Char. Capacitance Tol. Vol. 7 = 16 V 2F = Y5V 105 = 1000000 M = 20% pF; the third digit Z = -20% /+80% 8 = 25 V 9 = 50 V signifies the multiplying factor: Termination B = NiSn 2 = x 100 3 = x 1000 4 = x 10 000 5 = x 100 000 Packing Marking Series 2 = 180 mm; 7" paper 3 = 330 mm; 13" paper B = 180 mm; 7" blister F = 330 mm; 13" blister P = bulk case 0 = no marking D = BME 6 = x 1 000 000 2005 Dec 26 Rev.11 6 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V ELECTRICAL CHARACTERISTICS Class 2 capacitors; Y5V dielectric; NiSn terminations Unless otherwise stated all electrical values apply at an ambient temperature of 25 1 C, an atmospheric pressure of 86 to 105 kPa, and a relative humidity of 63 to 67%. DESCRIPTION VALUE Capacitance range (E6 series); note 1 10 nF to 10 F Tolerance on capacitance after 1000 hours 20% (M); -20% to +80% (Z) Tan ; note 1: all 25 V and 50 V except 0805 330 nF; 0603 /100 nF; 1206 /1 F; 1210 /10 F 5% sizes 0805 / 330 nF; 0603 / 100 nF; 1206 /1 F 7% 25 V 0805 470 nF 9% 1210 /10 F 12.5% all 16 V except 0402; 0603 330 nF; 0805 1.5 F; 1206 3.3 F; 1210 /10 F 9% sizes 0402; 0603 330 nF; 0805 1.5 F; 1206 3.3 F; 1210 /10 F 12.5% Rins >10 G or Rins x C 500 seconds whichever is less Insulation resistance after 1 minute at UR (DC): Maximum capacitance change with respect to capacitance at 25 C (for typical values see Fig.5) +22% to -82% Ageing typical 7% per time decade Resistance to soldering heat 260 C; 10 seconds Note 1. Measured at 25 C, 1 V, 1 kHz, using a four-gauge method. 2005 Dec 26 Rev.11 7 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V MBD076 0 C C (%) MBD078 2000 tan (x 10 4 ) 20 1500 40 1000 60 80 500 100 10 0 Fig.3 C C (%) 20 30 40 50 V DC (V) 0 25 Typical capacitance change with respect to the capacitance at 1 V as a function of DC voltage at 25 C. Fig.4 0 25 50 75 100 T ( oC) Typical tan as a function of temperature. MBD077 25 0 25 50 75 100 25 Fig.5 0 25 50 75 100 T ( oC) Typical capacitance change as a function of temperature. 2005 Dec 26 Rev.11 8 www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V TESTS AND REQUIREMENTS Table 2 Test procedures and requirements IEC 60384-10/ CECC 32 100 CLAUSE IEC 60068-2 TEST METHOD TEST PROCEDURE REQUIREMENTS 4.4 mounting the capacitors may be mounted on printed-circuit boards or ceramic substrates by applying wave soldering, reflow soldering (including vapour phase soldering) or conductive adhesive no visible damage 4.5 visual inspection and dimension check any applicable method using x10 magnification in accordance with specification 4.6.1 capacitance f = 1 kHz; Y5V measuring voltage 1 Vrms at 25 C within specified tolerance 4.6.2 tan f = 1 kHz; Y5V measuring voltage 1 Vrms at 25 C in accordance with specification 4.6.3 insulation resistance at UR (DC) for 1 minute RiCR 500 s 4.6.4 voltage proof 2.5 x UR for 1 minute no breakdown or flashover 4.7.1 temperature coefficient between minimum and maximum temperature in accordance with specification 4.8 adhesion a force of 5 N applied for 10 s to the line joining the terminations and in a plane parallel to the substrate no visible damage 4.9 bond strength of plating on end face mounted in accordance with IEC 60384-1, paragraph 4.35 no visible damage conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm C/C: 30% preconditioning: the terminations shall be well tinned after recovery C/C: 20% 4.10 Tb resistance to soldering heat resistance to leaching 2005 Dec 26 Rev.11 120 to 150 C during 1 minute; 260 5 C for 10 0.5 s in a static solder bath 260 5 C for 30 1 s in a static solder bath 9 tan : original specification Rins: original specification using visual enlargement of x10, dissolution of the terminations shall not exceed 10% www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V IEC 60384-10/ CECC 32 100 CLAUSE IEC 60068-2 TEST METHOD 4.11 Ta solderability zero hour test, and test after storage (20 to 24 months) in original packing in normal atmosphere; unmounted chips completely immersed for 2 0.5 s in a solder bath at 235 5 C the terminations shall be well tinned 4.12 Na rapid change of temperature preconditioning: between minimum and maximum temperature, 5 cycles no visible damage after 48 hours recovery: damp heat, steady state initialization: 48 4 hours after UR at 40 C for 1 hour (for initial value measurement); 500 12 hours at 40 C; 90 to 95% RH; UR applied no visible damage after 48 hours recovery: C/C: +30%/-40% tan : 15% Rins: 500 M or RiCR 100 s, whichever is less damp heat; with UR load initialization: 48 hours after UR at 40 C; for 1 hour (for initial value measurement); 500 12 hours at 40 C; 90 to 95% RH; UR applied preconditioning: endurance initialization: 2 x UR at 85 C for 1 hour, (initial value measurement after 48 4 hours) ; 2 x UR at 85 C for 1000 hours recovery 48 4 hours at room temperature 4.14 Ca 4.15 2005 Dec 26 Rev.11 TEST PROCEDURE 10 REQUIREMENTS C/C: 20% UR at 40 C for 1 hour, after 48 hours recovery: C/C: +30%/-40% tan : 15% Rins: 500 M or RiCR 25 s, whichever is less after 48 hours recovery: C/C: +30%/-40% tan : 15% Rins: 1000 M or RiCR 50 s, whichever is less www.yageo.com Phycomp Product specification Surface-mount ceramic multilayer capacitors Class 2, Y5V 16/25/50 V REVISION HISTORY Revision Date Change Notification Description Rev.11 Dec 26, 2005 Revised thickness of Y5V 0805 25/50 V 0.33 F Rev 10 Sep 21, 2005 - Y5V 0805 16 V thickness revised and range extended from 2.2 F to 4.7 F Rev.9 June 24, 2005 - - Revised thickness of: Y5V 1206 16 V from 4.7 F to10 F Y5V1206 25 V from 2.2 F to 10 F Rev.8 Jan 13, 2005 - - Revised thickness of Y5V 0805 16 V 1 F and Y5V 0805 25 V 470 nF to 1 F Rev.7 Jul 08, 2003 - - Updated company logo 2005 Dec 26 Rev.11 11 www.yageo.com