Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors GMC SERIES Introduction Multilayer Surface Mount Ceramic Capacitors are constructed by screen printing alternative layers of internal metallic electrodes onto ceramic dielectric materials and firing into a concrete monolithic body, then completed by application of metal end terminations which are fired to assure permanent bonding with the individual internal electrodes. Multilayer ceramic capacitors have various features such as large capacitance values in small sizes and excellent high frequency characteristics. Moreover, chip capacitors can be used on surface mount assembly equipment. Our fully integrated manufacturing and total quality control systems ensure unprecedented high standards of quality and reliability. Chip Capacitor Selection Selection of the most suitable capacitor for any application is based on the following: Dielectric Type The choice of dielectric is largely determined by the temperature stability required. COG (NPO) Capacitance change with temperature is 0-30ppm/C which is less than -0.3%C from -55C to +125C. Typical capacitance change with life is less than -0.1% for NPOs, one-fifth that shown by most other dielectrics. NPO formulations show no aging characteristics. X7R/X5R Its temperature variation of capacitance is within 15% from -55C to +125C (-55C to +85C for X5R). The capacitance change is non-linear. Z5U Despite their capacitance instability, Z5U formulations are very popular because of their small size, temperature range low ESL, low ESR and excellent frequency response. These features are particularly important for decoupling application where only a minimum capacitance value is required. Y5V Y5V formulations are for general purpose use in a limited temperature range. They have a wide temperature characteristic of +22% - 82% capacitance change over the operating temperature range of -30C to +85C. Y5Vs high dielectric constant allows the manufacture of very high capacitance values (up to 22MF) in small physical sizes. Capacitance Value & Tolerance Determined by circuit requirements. Note that chip prices decrease with lower capacitance value and looser tolerance. Voltage Determined by circuit requirements. Units are designed to exceed the withstanding voltage specification, i.e., the user need not incorporate an additional safety margin. Capacitor Size Select the smallest unit permitted by the circuit constraints that provides the required capacitance and voltage rating. All Cal-Chip capacitors conform to EIA specifications. Capacitor Termination Nickel barrier is standard and recommended for units exposed to repeated solder cycles, to minimize leaching of the termination. 1 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors Construction Solder plate; 100% matte SN; typical thickness 0.003mm to 0.005mm *(please see note) Nickel Barrier Layer (50 Micro-inches Electroplated Nickel min.) Inner Electrodes Example GMC21 CG 102 J 50 N T Size Code Dielectric Capacitance (pF) Capacitance Tolerance (EIA Code) Voltage Termination Packaging Code CG (COG) (NPO) X7R or X5R Z5U Y5V Capacitance values are represented in 3 digits, and expressed in pF. The first two digits are significant, and the third is the number of zeros. The letter "R" is used as a decimal point. 0R5 5R0 100 101 102 103 104 105 106 GMC02 = 0201 GMC04 = 0402 GMC10 = 0603 0.5pF 5pF 10pF 100pF 1000pF .01uF .1uF 1.0uF 10uF GMC21 = 0805 GMC31 = 1206 GMC32 = 1210 B C D F G J K M Z 0.1pf for < 10pF 0.25pF for < 10pF 0.5pF for < 10pF 1% 2% 5% 10% 20% -20%~+80% 6r3 10 16 25 50 100 200 N 6.3 DC 10 DC 16 DC 25 DC 50 DC 100 DC 200 DC Nickel Barrier NX* - Optional "SoftTerm" Available in select values, contact your sales associate for more information GMC40 = 1808 GMC43 = 1812 GMC45 = 1825 T* Tape and Reel *Optional "TD" designates large 10 inch or 13 inch reels - see packaging on pg.13 & 14 GMC55 = 2220 GMC57 = 2225 Note: Calchip has completed the Lead-Free transition. All parts shipped with or without the "custom designator" LF at the end of the part number will be Lead-Free. Lead-Free material will still continue to have an LF at the end of the Lot Code and a green RoHS symbol on the label. Please contact your sales associate if you require non-RoHS material. 2 M Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors 0201 GMC02 DIMENSION (MM) 0.6 r 0.03 0.3 r 0.03 0.3 r 0.03 0.15 r 0.05 L(L1) W H BW(L2/L3) dielectric Rated Voltage Cap. Range 0.5pF 0R5 1.0 1R0 1.2 1R2 1.5 1R5 1.8 1R8 2.2 2R2 2.7 2R7 3.3 3R3 3.9 3R9 4.7 4R7 5.6 5R6 6.8 6R8 8.2 8R2 10 100 12 120 15 150 18 180 22 220 27 270 33 330 39 390 47 470 56 560 68 680 82 820 100 101 120 121 150 151 180 181 220 221 270 271 330 331 390 391 470 471 560 561 680 681 820 821 1.0nF 102 1.2 122 1.5 152 1.8 182 2.2 222 2.7 272 3.3 332 3.9 392 4.7 472 5.6 562 6.8 682 8.2 822 10 103 12 123 15 153 18 183 22 223 27 273 33 333 39 393 47 473 56 563 68 683 82 823 100 104 120 124 150 154 180 184 220 224 270 274 330 334 390 394 470 474 560 564 680 684 820 824 1.0uF 105 2.2 225 3 NPO/COG 25 X5R 6.3 10 6.3 H L3 L2 W L1 X7R 10 16 Y5V/Z5U 6.3 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors 0402 & 0603 GMC04 Type Length (L1) Width (W) mm inches mm inches Thickness (H) mm inches Termination Band (L2+L3) mm inches Dielectric Cap Range 0.5pF 1.0 1.2 1.5 Code 0R5 1R0 1R2 1R5 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 150 220 270 330 390 470 560 680 820 1.0uF 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 15 22 33 47 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 154 224 274 334 394 474 564 684 824 105 225 275 335 395 475 565 685 825 106 156 226 336 476 0603 1.0r0.05 0.04r0.002 0.5r0.05 0.02r0.002 0.5r0.1 0.02r0.004 1.6r0.2 0.063r0.008 0.8r0.2 0.031r0.008 0.8r0.2 0.031r0.008 Min 0.1 0.004 Max 0.35 0.014 Band Gap (L4)mm (Min) inches Rated Voltage d.c. GMC10 0402 Min 0.1 0.004 0.3 0.012 COG 25 50 X5R 6.3 10 0.6 0.015 X7R 16 6.3 10 16 Max 0.4 0.015 Y5V & Z5U 25 50 6.3 10 16 25 COG 50 25 X5R X7R Y5V & Z5U 50/ 50 100 6.3 10 16 6.3 10 16 25 100 6.3 10 25 50 H L2 4 16 L4 L3 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors COG/NPO GMC21 GMC31 GMC32 GMC40 GMC45 GMC55 0805 1206 1210 1808 1812 1825 2220 2225 2.0r0.3 0.08r0.012 1.25r0.2 0.05r0.008 1.3 0.051 Min Max 0.25 0.75 0.01 0.03 0.5 0.019 3.2r0.3 0.125r0.012 1.6r0.2 0.063r0.008 1.6 0.063 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.2r0.3 0.125r0.012 2.5r0.3 0.10r0.012 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.57r0.25 0.18r0.01 2.03r0.25 0.08r0.01 2.03 0.08 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.5r0.35 0.18r0.014 3.2r0.3 0.125r0.012 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.5r0.35 0.18r0.014 6.3r0.4 0.25r0.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.7r0.4 0.225r0.016 5.0r0.4 0.197r0.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.7r0.4 0.225r0.016 6.3r0.4 0.25r0.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 50/63 50/63 50/63 50/63 50/63 Type Length mm (L1) Inches Width mm (W) Inches Thick(Max) mm (H) Inches Termination Band mm (L2+L3) Inches Band Gap mm (L4) Inches Rated Voltage d.c. Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.0 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 100 5 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R0 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 107 16 25 50 25 50 16 25 50/63 GMC43 GMC57 H L2 L4 L3 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors COG/NPO (cont.) GMC31 GMC32 GMC40 GMC43 GMC45 GMC55 Type GMC21 0805 1206 1210 1808 1812 1825 2220 2225 Length (L1) mm Inches Width (W) mm Inches Thick(Max) mm (H) Inches Termination Band (L2+L3) mm Inches Band Gap mm (L4) Inches Rated Voltage d.c. 2.00.3 0.080.012 1.250.2 0.050.008 1.3 0.051 Min Max 0.25 0.75 0.01 0.03 0.5 0.019 3.20.3 0.1250.012 1.60.2 0.0630.008 1.6 0.063 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.20.3 0.1250.012 2.50.3 0.100.012 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.570.25 0.180.01 2.030.25 0.080.01 2.03 0.08 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.50.35 0.180.014 3.20.3 0.1250.012 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.50.35 0.180.014 6.30.4 0.250.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.70.4 0.2250.016 5.00.4 0.1970.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.70.4 0.2250.016 6.30.4 0.250.016 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 100 100 100 100 100 100 100 100 200 L4 L3 Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 68 100 6 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 686 107 200 200 200 200 200 200 200 GMC57 H L2 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors X7R Type GMC21 GMC31 GMC32 0805 1206 1210 1808 1812 1825 2220 2225 3.2r0.3 0.125r0.012 2.5r0.3 0.10r0.012 2.8 0.110 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.57r0.25 0.18r0.01 2.03r0.25 0.08r0.01 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.5r0.35 0.18r0.014 3.2r0.3 0.125r0.012 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.5r0.35 0.18r0.014 6.3r0.4 0.25r0.016 3.2 0.126 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.7r0.4 0.225r0.016 5.0r0.4 0.197r0.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.7r0.4 0.225r0.016 6.3r0.4 0.25r0.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 10 10 10 10 10 10 Length(L1) mm 2.0r0.3 3.2r0.3 Inches 0.08r0.012 0.125r0.012 Width (W) mm 1.25r0.2 1.6r0.2 Inches 0.05r0.008 0.063r0.008 Thick(Max) mm 1.5 1.8 (H) Inches 0.059 0.071 Termination Band Min Max Min Max 0.25 0.75 0.25 0.75 (L2+L3) mm Inches 0.01 0.03 0.01 0.03 Band Gap mm 0.5 1.4 (L4) Inches 0.019 0.055 Rated Voltage d.c. 6.3 10 16 25 6.3 10 16 25 Cap. Range Code 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 68 100 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 686 107 7 16 25 GMC40 16 GMC43 25 16 25 GMC45 16 25 GMC55 16 25 GMC57 16 25 H L2 L4 L3 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors X7R (cont) GMC21 GMC31 GMC32 GMC40 GMC43 0805 1206 1210 1808 1812 1825 2220 2225 2.00.3 0.080.012 1.250.2 0.050.008 1.3 0.051 Min Max 0.25 0.75 0.01 0.03 0.5 0.019 3.20.3 0.1250.012 1.60.2 0.0630.008 1.8 0.063 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.20.3 0.1250.012 2.50.3 0.100.012 2.8 0.07 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.570.25 0.180.01 2.030.25 0.080.01 3.0 0.08 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.50.35 0.180.014 3.20.3 0.1250.012 3.0 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.50.35 0.180.014 6.30.4 0.250.016 3.2 0.07 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.70.4 0.2250.016 5.00.4 0.1970.016 3.5 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.70.4 0.2250.016 6.30.4 0.250.016 3.5 0.07 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 50 50 50 50 50 50 50 50 100 200 L4 L3 Type Length(L1) mm Inches Width (W) mm Inches Thick(Max) mm (H) Inches Termination Band (L2+L3) mm Inches Band Gap mm (L4) Inches Rated Voltage d.c. Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 8 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 100 200 100 200 100 200 100 200 100 200 GMC45 100 200 GMC55 100 200 GMC57 H L2 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors X5R GMC21 GMC31 GMC40 GMC43 GMC45 GMC55 0805 1206 1210 1808 1812 1825 2220 2225 2.00.3 0.080.012 1.250.2 0.050.008 1.5 0.059 Min Max 0.25 0.75 0.01 0.03 0.5 0.019 3.20.3 0.1250.012 1.60.2 0.0630.008 1.8 0.070 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.20.3 0.1250.012 2.50.3 0.100.012 2.8 0.110 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.570.25 0.180.01 2.030.25 0.080.01 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.50.35 0.180.014 3.20.3 0.1250.012 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.50.35 0.180.014 6.30.4 0.250.016 3.2 0.126 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.70.4 0.2250.016 5.00.4 0.1970.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.70.4 0.2250.016 6.30.4 0.250.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 6.3 10 16 25 6.3 10/16 25 N/A 6.3 6.3 6.310/1625 Type Length(L1) mm Inches Width (W) mm Inches Thick(Max) mm (H) Inches Termination Band (L2+L3) mm Inches Band Gap mm (L4) Inches Rated Voltage d.c. Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 100 9 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 107 6.3 10 16 GMC32 10 16 10 16 GMC57 16 25 H L2 L4 L3 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors Y5V/Z5U GMC21 GMC31 GMC40 GMC43 0805 1206 1210 1808 1812 1825 2220 2225 2.0r0.3 0.08r0.012 1.25r0.2 0.05r0.008 1.5 0.059 Min Max 0.75 0.25 0.03 0.01 0.5 0.019 3.2r0.3 0.125r0.012 1.6r0.2 0.063r0.008 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.2r0.3 0.125r0.012 2.5r0.3 0.10r0.012 2.8 0.110 Max Min 0.25 0.75 0.01 0.03 1.4 0.055 4.57r0.25 0.18r0.01 2.03r0.25 0.08r0.01 3.0 0.118 Min Max 0.75 0.25 0.03 0.01 2.0 0.078 4.5r0.35 0.18r0.014 3.2r0.3 0.125r0.012 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.5r0.35 0.18r0.014 6.3r0.4 0.25r0.016 3.2 0.126 Max Min 0.25 0.75 0.01 0.03 2.2 0.087 5.7r0.4 0.225r0.016 5.0r0.4 0.197r0.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.7r0.4 0.225r0.016 6.3r0.4 0.25r0.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 Type Length(L1) mm Inches Width (W) mm Inches Thick(Max) mm (H) Inches Termination Band (L2+L3) mm Inches Band Gap mm (L4) Inches Rated Voltage d.c. Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 68 100 10 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 686 107 6.3 10 16 25 6.3 10 GMC32 16 25/35 6.3 10 16 25/35 6.3 10 16 25 6.3 10 GMC45 16 25/35 6.3 10 16 25 GMC55 6.3 10 16 GMC57 25 6.3 10 16 25 H L2 L4 L3 W L1 Cal-Chip Electronics, Incorporated Multilayer Ceramic Chip Capacitors Y5V/Z5U (cont) GMC21 GMC31 GMC32 GMC40 GMC43 0805 1206 1210 1808 1812 1825 2220 2225 2.00.3 0.080.012 1.250.2 0.050.008 1.5 0.059 Min Max 0.25 0.75 0.01 0.03 0.5 0.019 3.20.3 0.1250.012 1.60.2 0.0630.008 1.8 0.07 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 3.20.3 0.1250.012 2.50.3 0.100.012 2.8 0.110 Min Max 0.25 0.75 0.01 0.03 1.4 0.055 4.570.25 0.180.01 2.030.25 0.080.01 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.0 0.078 4.50.35 0.180.014 3.20.3 0.1250.012 3.0 0.118 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 4.50.35 0.180.014 6.30.4 0.250.016 3.2 0.126 Min Max 0.25 0.75 0.01 0.03 2.2 0.087 5.70.4 0.2250.016 5.00.4 0.1970.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 5.70.4 0.2250.016 6.30.4 0.250.016 3.5 0.138 Min Max 0.25 0.75 0.01 0.03 2.9 0.114 50 50 50 50 50 50 50 50 100 200 L4 L3 Type Length (L1) mm Inches Width (W) mm Inches Thick(Max) mm (H) Inches Termination Band (L2+L3) mm Inches Band Gap mm (L4) Inches Rated Voltage d.c. Cap. Range 0.5pF 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0nF 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 560 680 820 1.0uF 2.2 3.3 4.7 6.8 10 22 33 47 68 100 11 Code 0R5 1R0 1R2 1R5 1R8 2R2 2R7 3R3 3R9 4R7 5R6 6R8 8R2 100 120 150 180 220 270 330 390 470 560 680 820 101 121 151 181 221 271 331 391 471 561 681 821 102 122 152 182 222 272 332 392 472 562 682 822 103 123 153 183 223 273 333 393 473 563 683 823 104 124 154 184 224 274 334 394 474 564 684 824 105 225 335 475 685 106 226 336 476 686 107 100 200 100 200 100 200 100 200 100 200 GMC45 100 200 GMC55 100 200 GMC57 H L2 W L1 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors COG Dielectric Ultra stable class I dielectric: linear temperature coefficient, low loss, negligible change of electrical properties with time, voltage and frequency. Operating Temperature Range Temperature Coefficient -55C to +125C 030ppmC Temperature Voltage Coefficient (cMax @ VDCW) 030ppm/C Dissipation Factor Insulation Resistance 0.1% Max, * 25C, VDCW:: 0.02% Typical >100GF or 1000F, whichever is less *125C, VDCW: >10GF or 100F whichever is less Dielectric withstanding Voltage 3 X VDCW Aging Rate 0% per decade hour Test Parameters * C1000pF f=1MHz V=1.0Vrms 0.2Vrms T=25C * C>1000pF f=1KHz V=1.0Vrms 0.2Vrms T=25C X7R/X5R Dielectric Stable class II dielectric Operating Temperature Range Temperature Coefficient -55C X7R = to to -55C +125C +125C 15% X5R = -55C to +85C 12 Temperature Voltage Coefficient (cMax @ VDCW) X7R X7R/X5R Not Applicable Applicable Not Dissipation Factor Insulation Resistance 2.5% Max, * 25C, VDCW:: 1.8% Typical >100GFor 1000F, whichever is less *125C, VDCW: >10GF or 100F whichever is less Dielectric withstanding Voltage 2.5 X VDCW Aging Rate <2% per decade hour Test Parameters 1KHz, 1.0Vrms 0.2Vrms 25C values > or = to 10uF 1.0Vrms 120Hz Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors - Z5U (Y5V) Dielectric High capacitance per unit volume: general purpose product Operating Temperature Range -30C to +85C Temperature Coefficient Dissipation Factor Insulation Resistance +22% -82% 3.0% Max, 2.0% Typical 10G or 100F whichever is less, 25C, VDCW Packaging (Taping) Dielectric withstanding Voltage Test Parameters Aging Rate 3.0% per decade hour 2.5 X VDCW 1KHz, 1Vrms 25C values > or = to 10uF 1.0Vrms 120Hz Standard Reel (Reel Type-Size) Unit:mm A B C D E W t R o178 2.0 o50 min. o13.0 0.5 o21.0 0.8 2.0 0.5 14.9 1.5 0.8 0.2 1.0 "TD" designator for OPTIONAL optional 10/13 inch reels 10000 units per reel Unit:mm A B C D E W t R o250 2.0 o50 min. o13.0 0.5 o21.0 0.8 2.0 0.5 10.0 1.5 0.8 0.2 1.0 Carrier Tape (Standard) Top Cover Tape * To peel off the cover tape by the method shown in the right figure apply a peel-off force of 20 gf - 60 gf (card board); 35 gf - 75 gf (plastic tape). * The cover tape should not touch the top or bottom of the chip. Empty section Chip Mounting section Bottom Cover Tape Empty section Leader section { { * Follow the illustration for the start and end of the winding operation. Tape unreeling direction { * If the cover tape has been peeled off from the top, stick it back on with a suitable adhesive. Cover Tape tension direction { * If the cover tape has been peeled off it may be difficult to remove the chip due to punch-hole clearance, dirt, and debris. Make sure therefore that no paper waste will adhere to and block the absorption nozzle. 165-180 Carrier Tape Start 50 pitch (200mm) 30 pitch (120mm) Unreeling direction 200mm 13 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors * Cardboard carrier tape for 0402,0603 type and 0805/1206 type Type A B 0402 0603 0805 1206 0.70.2 1.10.2 1.650.2 2.00.2 1.30.2 1.90.2 2.40.2 3.60.2 W F E P1 P2 Unit: mm P0 t1 D0 t2 8.00.3 3.50.05 1.750.1 4.00.1 2.00.05 4.00.1 o1.5+0.1 1.1 max 1.4 max Mounting Hole Angular Punch Hole Std Reel Qty. 7in (10/13in)* 10,000 (20,000) 4,000 (10,000) 4,000 (10,000) 4,000 (10,000) *quantities listed are considered as "standard" and subject to change * Embossed plastic carrier tape for 0805/1206 type and 1210 type Type 0805 1206 1210 A B 1.450.2 2.30.2 2.00.2 3.60.2 2.90.2 3.60.2 W F E P1 P2 P0 Unit: mm D0 t1 t2 8.00.3 3.50.05 1.750.1 4.00.1 2.00.05 4.00.1 o1.5+0.1 0.6 max 2.5 max -0 Mounting Hole Angular Embossed Hole Std Reel Qty. 7in (10/13in)* 3,000 (10,000) 2,500 (10,000) 2,000 (4,000) *quantities listed are considered as "standard" and subject to change * Embossed plastic carrier tape for 1812,1825,2220 and 2225 type Type A B 1812 1825 2220 2225 3.60.2 6.80.3 5.50.3 6.80.3 4.90.2 4.90.2 6.20.3 6.20.3 W F E 12.00.3 5.50.05 1.750.1 Unit: mm P1 P2 P0 8.00.1 2.00.05 4.00.1 D0 t1 t2 Mounting Hole Angular o1.50.1 0.6 max. 6.5 max. Embossed Hole Std Reel Qty. 7in (10/13in)* 1,000 (2,000) 1,000 (1,500) 1,000 (1,500) 500 (1,000) *quantities listed are considered as "standard" and subject to change 14 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors RELIABILITY AND TEST CONDITIONS Item Specification Capacitance Within tolerance shown by part number code * Class (I) C<30pF:Q400+20xC C30pF:Q1000 * Class (II) X7R/X5R:DF2.5% Y5V/Z5U:DF3.0% Dissipation Factor (tan or Q) NPO thru X5R: C50,000pF: IR100G C>50,000pF: IR500M. Per Uf. Y5V/Z5U: IR10G Insulation Resistance(IR) Dielectric Withstanding Voltage There shall be no evidence of damage or flash over during the test Termination Adherence No mechanical damage Test Method * Class (I) C<1000pF:1MHz10%, 0.5 to 5Vrms C1000pF:1KHz10%, 1.00.2Vrms * Class (II) 1KHz10%, 1.00.2Vrms values > or = to 10uF 1.0Vrms 120Hz Apply rated voltage for 60 seconds at room temperature and normal humidity. (70% RH max) Apply 3 x rated voltage (Class I) or 2.5 x rated voltage (Class II) to both terminations for 5 seconds. Charge and discharge current are less than 50mA. Care shall be taken to avoid thermal shock. 500g of steady pull is applied in direction of arrow for 1 minute. Bend Strength No mechanical damage Life Test (High Temperature Loading Test) * Class (I) No more than 3% or 0.3pF whichever is less * Class (II) X7R/X5R:10% max Y5V/Z5U:30% max C Q or DF IR * Class (I) C<10pF:Q>200+10xC 10C<30pF:Q275+5/2xC C30pF:Q350 * Class (II) X7R/X5R:DF5.0% Y5V/Z5U:DF7.5% 1000M or 50F, min whichever is less After soldering capacitor on the glass-epoxy PWB, 2 mm of vending shall be applied for 10 seconds as shown by drawing. Applied 2 x rated voltage at maximum operating temperature for 1000 hours. The surge current shall not exceed 50mA after above testing condition, test samples shall be kept in room temperature for 24 hours (Class I) or 48 hours (Class II), and then shall be measured. 15 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors RELIABILITY AND TEST CONDITIONS Item Specification Moisture Test C Q or DF IR Moisture Resistance Test C * Class (I) No more than 2.5% or 0.25pF whichever is larger * Class (II) X7R/X5R:5% Y5V/Z5U:20% Q or DF To satisfy the specified initial value. IR Solderability Resistance to Solder Heat Test C Q or DF IR The capacitors shall be subjected to 40C, 90-95%RH for 500 hours. After above testing condition, samples shall be kept in room temperature for 24 hours (Class I) or 48 hours (Class II), and then shall be measured. 1000M or 50F, whichever is less * Class (I) No more than 7.5% or 0.75pF whichever is larger C * Class (II) X7R/X5R:10% Y5V/Z5U:30% * Class (I) C<30pF:Q>100+100/3xC Q C30pF:Q200 or * Class (II) DF X7R/X5R:DF5.0% Y5V/Z5U:DF7.5% 500M or 25F, min IR whichever is less Temperature Cycle 16 * Class (I) No more than 5% or 0.5pF whichever is larger * Class (II) X7R/X5R:10% Y5V/Z5U:30% * Class (I) C<10pF:Q>200+10xC 10C<30pF:Q275+5/2xC C30pF:Q350 * Class (II) X7R/X5R:DF5.0% Y5V/Z5U:DF7.5% Test Method To satisfy the specified initial value. Termination area shall be at least 95% covered with a new solder coating. There shall be no crack and ceramic exposure of terminated surface by melting. * Class (I) No more than 2.5% or 0.25pF whichever is larger * Class (II) X7R/X5R:5% Y5V/Z5U:20% To satisfy the specified initial value. To satisfy the specified initial value. Apply rated voltage at 40C, 90-95%RH for 500 hours. The surge current shall not exceed 50mA. After testing with above condition, samples shall be kept in room temperature for 24 hours (Class I) or 48 hours (Class II), and then shall be measured. Perform 5 cycles as follow: 1. Room temperature. Dwell for 15 minutes. 2. Minimum operating temperature, dwell for 30 minutes. 3. Room temperature, dwell for 30 minutes. 4. Maximum operating temperature, dwell for 30 minutes. After above testing condition, samples shall be kept in room temperature for 24 hours (Class I) or 48 hours (Class II), and then shall be measured. The capacitors are completely immersed during 40.5 seconds in the molten solder with a temperature of 2305C *Solder: Sn 63. Immerse into molten solder at 2705C for 30.5 seconds. Preheat before immersion. 1. 80~100C for 2 minutes. 2. 150~180C for 2 minutes. 3. 2705C for 30.5 seconds. The capacitance measurement shall be made after sample keeping at room temperature for 24 hours. Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors APPLICATION MANUAL FOR SURFACE MOUNTING 1. Temperature / Humidity Control Since dew condensation may occur by the differences in temperature when the products are take out of storage, it is important to maintain a temperaturecontrolled environment. 2. Design of Solder Land Pattern When designing printed circuit boards, the shape and size of the solder lands must allow for the proper amount of solder on the capacitor. The amount of solder at the end terminations has a direct effect on the probability that the chip will crack. The greater amount of solder, the larger amount of stress on the chip, and the more likely that it will break. Use the following illustrations as guidelines for proper solder land design. Recommendation of solder land shape and size. 3. Adhesives MLCCs generally require the use of an adhesive to adhere the chips to the circuit board prior to wave soldering. 3-1. Requirements for Adhesives - They must have enough adhesion so that the chips will not fall off or move during the handling of the circuit board. - They must maintain their adhesive strength when exposed to soldering temperatures. - They should not spread or run when applied to the circuit board. - They should have a long pot life. - They should harden quickly. - They should not corrode the circuit board or chip material. - They should be a good insulator. - They should be non-toxic, and not produce harmful gases, nor be harmful when touched. 3-2. Application Method It is important to use the proper amount of adhesive. Too little will cause poor adhesion to the circuit board, and too much may strain the conductor pattern, thereby causing defective soldering. The following illustrations show the proper quantity of adhesive. (Unit: mm) Type 21 31 a 0.2 min 0.2 min b 70~100m 70~100m c >0 >0 3-3. Adhesive Hardening Characteristics To prevent oxidation of the terminations, the adhesive must harden at 160C or less, within 2 minutes or less. 17 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors 4. Mounting 4-1. Mounting Head Pressure Excessive pressure will cause chip capacitors to crack. The pressure between nozzle and chip capacitor will be 300g maximum during mounting. 4-2.Bending Stress Bending of printed circuit board by mounting head when double-sided circuit boards are used, chip capacitors first are mounted and soldered onto one side of the board. When the capacitors are mounted onto the other side, it is important to support the board as shown in the illustration. If the circuit board is not supported, it may bend, causing the already installed capacitors to crack. 5. Flux Although highly activated flux gives better solderability, substances which increase activity may also degrade the insulation of the chip capacitors. To avoid such degradation, it is recommended that a mildly activated rosin flux (less than 0.2% chlorine) be used. 6. Soldering Since a multilayer chip ceramic capacitor comes into direct contact with melted solder during soldering, it is exposed to potentially damaging mechanical stress caused by the sudden temperature change. The capacitor may also be subject to silver migration, and to contamination by the flux. Because of these factors, soldering technique is critical. 6-1. Soldering Methods Method Reflow Soldering Flow Soldering Classification Mass reflow * IR/Convection * VPS (Vapor phase) Selective reflow * Hot air/gas * Laser Dual Wave 6-2. Soldering Profile To avoid the crack problem by sudden temperature change, follow the temperature profile in graph 64. 18 Multilayer Ceramic Chip Capacitors GMC SERIES 6-3 Flux selection Soldering Although highly-activated flux gives better solderability, substances which increase activity may (Continued) also degrade the insulation of the chip capacitors. To avoid such degradation, the following is recommended. 1) It is recommended to use a mildly activated rosin flux (less than 0.1 wt% chlorine). Strong flux is not recommended. 2) Excessive flux must be avoided. Please provide proper amount of flux. 3) When water-soluble flux is used, enough washing is necessary. 6-4 Recommended soldering profile by various methods IR reflow soldering profile Wave soldering profile 4 / sec max Over 60sec at least by natural cooling Recommended IR reflow soldering profile for SMT process with SnAgCu series solder paste. Manual soldering (solder iron) 19 Recommended wave soldering profile for SMT process with SnAgCu series solder. # Wave soldering is recommended only for the following case sizes: 0603(1608); 0805(2012)&1206(3216) thickness< 1mm Multilayer Ceramic Chip Capacitors GMC SERIES Soldering 6-5 Avoiding thermal shock (Continued) 1) Preheating condition Soldering Wave soldering Reflow soldering Manual soldering Temperature difference( T) Size 1206 1206 1210 1206 1210 (3216) (3216) (3225) (3216) (3225) or or or or or less less more less more T T T T T 150 190 130 190 130 2) Cooling condition Natural cooling using air is recommended. If the chips are dipped into a solvent for cleaning, the temperature difference (T) must be less than 100. 6-6 Amount of solder Excessive solder will induce higher tensile force in chip capacitor when temperature changes and may result in chip cracking. Insufficient solder may detach the capacitor from the P.C. board. 6-7 Solder repair by solder iron 1) Selection of the soldering iron tip Tip temperature of solder iron varies by its type, P.C. board material and solder pad size. Higher tip temperature may be faster, but the heat shock may crack the chip capacitor. (Following conditions are recommended.) Temp. () 300 Max Wattage (W) 20 Max Shape (mm) 3.0 Max 2) Direct contact of the soldering iron with ceramic dielectric of chip capacitor may cause cracking. Do not make contact directly with the ceramic dielectric. 20 Cal-Chip Electronics, Incorporated GMC SERIES Multilayer Ceramic Chip Capacitors APPLICATION INFORMATION ON SOLDER PAD DESIGN FOR SURFACE MOUNT CHIP CAPACITOR Recommended Pad Dimensions Dimensions (inches) Chip Size L W S T 0402* 0.021 0.022 0.017 0.059 0603* 0.035 0.030 0.030 0.100 0805 0.040 0.050 0.040 0.120 1206 0.040 0.065 0.080 0.160 1210 0.040 0.100 0.080 0.160 1812* 0.050 0.120 0.130 0.230 1825* 0.050 0.250 0.130 0.230 2220 0.050 0.250 0.130 0.230 2225* 0.050 0.250 0.170 0.270 3640* 0.060 0.400 0.300 0.420 *These sizes are recommended for use with IR and vapor phase soldering only. NOTICE: Specifications are subject to change without notice. Contact your nearest Cal-Chip Sales Office for the latest specifications. All statements, information and data given herein are believed to be accurate and reliable, but are presented without guarantee, warranty, or responsibility of any kind, expressed or implied. Statements or suggestions concerning possible use of our products are made without representation or warranty that any such use is free of patent infringement and are not recommendations to infringe any patent. The user should not assume that all safety measures are indicated or that other measures may not be required. Specifications are typical and may not apply to all applications. 21